Static tensile test and tensile-tensile fatigue test of medium carbon steel sheet specimens with surface crack precut were performed on MTS810 hydraulic testing machine to clear the meaning of the point of Hp( y ) value zero. Magnetic memory signals were measured during the test process. The results show that only one point of Hp( y ) zero value exists in all measured magnetic signal curves during the loading process, which should be a sign of intersection of positive-negative magnetic poles after magnetic ordered state appears and does not indicate the position of surface crack precut. The analysis shows that the surface crack precut can not interrupt the magnetic ordered state occurred during the test completely, hence its Hp( y ) value is not zero. However, the crack extending to a penetrated defect at the instant of specimen's fracture leads to the discontinuance of magnetic ordered state.
参考文献
| [1] | Doubov A A .Technique for monitoring the bends of boiler and steam-line tubes using the magnetic memory of metal[J].Thermal Engineering,2001,48(04):289. |
| [2] | Chechko Π .Using the method of magnetic memory of metal to evaluate the service life of the items of power equipment at the Konakovo district power station[J].Thermal Engineering,2002,49(12):1028. |
| [3] | Doubov A A .Express method of quality control of a spot resistance welding with usage of metal magnetic memory[J].Welding in the Would,2002,46:317. |
| [4] | Doubov A A;Demin E A;Milyaev A I .The experience of gas pipeline stress-strain state control with usage of the metal magnetic memory method as compared with conventional methods and stress control means[J].Welding in the Would,2002,46(9-10):29. |
| [5] | DONG Li-hong,XU Bin-shi,DONG Shi-yun,CHEN Qun-zhi,WANG Yu-ya,ZHANG Lei,WANG Dan,YIN Da-wei.Metal magnetic memory testing for early damage assessment in ferromagnetic materials[J].中南工业大学学报（英文版）,2005(z2):102-106. |
| [6] | 张卫民,A A Doubov,孙海涛,刘红光.高强度钢磨削时的金属磁记忆现象初探[J].兵工学报,2005(03):375-378. |
| [7] | 任吉林,李晓刚,宋凯,唐继红,马宏伟.典型受载铁磁构件的数值模拟和磁特性[J].北京科技大学学报,2005(06):684-687. |
| [8] | 李路明,黄松岭,汪来富,杨海青,施克仁.Research on magnetic testing method of stress distribution[J].中国有色金属学会会刊(英文版),2002(03):388-391. |
| [9] | Tomohiro Yamasaki;Shinji Yamamoto;Masahiko Hirao .Effect of applied stresses on magnetostriction of low carbon steel[J].Ndt & E International,1996,29(05):263. |
| [10] | Richard M Hornreich;Harvey Rubinstein;Robert J Spain .Magnetostrictive phenomena in metallic materials and some of their device applications[J].IEEE Transactions on Magnetics,1971,7(01):29. |
| [11] | Bulte D P;Langman R A .Originsofmagnetomechanical effect[J].Journal of Magnetism and Magnetic Materials,2002,251:229. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%