为了控制钢卷氧化铁皮的厚度和结构,研究了工业生产条件下,钢卷卷取后的冷却工艺对510MPa级大梁钢氧化铁皮厚度和结构以及铁皮附着性的影响.结果表明:钢卷卷取后采用堆垛和加盖保温罩冷却时,氧化铁皮厚度在10～20 μm,氧化铁皮结构以Fe2O3和Fe3O4为主,氧化铁皮易于脱落；采用自然冷却和风机进行吹风冷却时,氧化铁皮较薄,厚度小于10μm,且氧化铁皮结构以共析Fe3O4和Fe为主,氧化铁皮的附着性较好.
参考文献
| [1] | 刘振宇,于洋,郭晓波,关菊,王国栋.板带热连轧中氧化铁皮的控制技术[J].轧钢,2009(01):5-9. |
| [2] | Taro KIZU;Yasunobu NAGATAKI;Toru INAZUMI .Effects of Chemical Composition and Oxidation Temperature on the Adhesion of Scale in Plain Carbon Steels[J].ISIJ International,2001(12):1494-1501. |
| [3] | S.G.Hayashi;T.Sekimoto;K.Honda et al.Effect of S and Mn on the high-temperature oxidation and scale spallation behavior of low-carbon steels steels[J].,2009,49(12):1938-1944. |
| [4] | R.Y.Chen;W.Y.D.Chen .Oxidation of Low-Carbon,Low-Silicon Mild Steel at 450-900 ℃ Under Conditions Relevant to Hot-Strip Processing[J].Oxidation of Metals,2002,57(01):53-79. |
| [5] | Vladimir V. BASABE;Jerzy A. SZPUNAR .Effect of O_2 in Heating Atmosphere on Hydraulic Descaling in Hot Rolling of Low Carbon Steel[J].ISIJ International,2008(4):467-474. |
| [6] | 王银军,穆海玲,董汉君,李欣波,张国河,沈鹏杰,杜献智.SPHC热带氧化铁皮酸洗困难原因分析及对策[J].轧钢,2006(04):51-54. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%