采用溶胶-凝胶法在经过扩孔处理的Al2O3基载体上制备了纳米ZrO2/Al2O3复合载体,并通过浸渍法制备了NiO/ZrO2/Al2O3催化剂. 用XRD,TPR,TPD和N2吸附等技术分别考察了载体和催化剂的结构及表面性能,研究了复合载体对Ni/ZrO2/Al2O3催化CO2重整CH4反应性能的影响. 结果表明,纳米ZrO2/Al2O3复合载体具有较大的比表面积、适宜的孔径分布及稳定的t-ZrO2结构,Ni/ZrO2/Al2O3催化剂具有较好的CO2重整CH4反应活性和稳定性.
参考文献
| [1] | Martinez R;Romero E;Guimon C;Bilbao R .[J].Applied Catalysis A:General,2004,274(1-2):139. |
| [2] | Erdohelyi A;Cserenyi J;Solymosi F .[J].Journal of Catalysis,1993,141(01):287. |
| [3] | Bradford M C J;Vannice M A .[J].Journal of Catalysis,1999,183(01):69. |
| [4] | Rostrup-Nielsen J R;Bak Hansen J H .[J].Journal of Catalysis,1993,144(01):38. |
| [5] | Souza M M V M;Aranda D A G;Schmal M .[J].Journal of Catalysis,2001,204(02):498. |
| [6] | Lercher J A;Bitter J H;Hally W;Niessen W,Seshan K .[J].Studies in Surface Science and Catalysis,1996,101A:463. |
| [7] | Tomishige K;Chen Y G;Fujimoto K .[J].Journal of Catalysis,1999,181(01):91. |
| [8] | Tsipouriari V A;Verykios X E .[J].Journal of Catalysis,1999,187(01):85. |
| [9] | Chen Y G;Tomishige K;Yokoyama K;Fujimoto K .[J].Journal of Catalysis,1999,184(02):479. |
| [10] | 李春林,伏义路,卞国柱.不同方法制备的Ni/ZrO2-CeO2-Al2O3催化剂对 CH4-CO2重整反应的催化性能[J].催化学报,2003(03):187-192. |
| [11] | 魏俊梅,徐柏庆,李晋鲁,程振兴,王亚权,朱起明.CO2重整CH4纳米ZrO2负载Ni催化剂的研究（Ⅰ）--与常规载体上Ni催化剂的比较[J].高等学校化学学报,2002(01):92-97. |
| [12] | 李艳,叶青,魏俊梅,徐柏庆.制备高效稳定CO2重整甲烷Ni/ZrO2催化剂的新方法[J].催化学报,2004(04):326-330. |
| [13] | 许峥,张鎏,张继炎,赵金保.超细镍基催化剂上CH4-CO2重整反应的性能Ⅱ.制备方法对催化性能和抗积碳性能的影响[J].催化学报,2000(04):309-313. |
| [14] | 陈吉祥,邱业君,张继炎,苏万华.La2O3和CeO2对CH4-CO2重整Ni/MgO催化剂结构和性能的影响[J].物理化学学报,2004(01):76-80. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%