HP40Nb steel,used as a candidate material for ethylene cracking furnace tube,suffers creep and carburization damage from the complex environment of high temperature,high carbon potential and low oxygen partial pressure,and they lead to failure of the furnace tubes ahead of designed life.In order to investigate damage evolution under the complex condition,coupled creep damage and carburization damage constitutive equations were developed according to continuum damage mechanics theory.Based on the finite element ABAQUS code,user subroutines were developed for analyzing damage evolution of ethylene furnace tube under the action of coupled creepcarburization.The results show that carburization accelerates the damage process dramatically,damage value reaches the critical value along the inner surface after serving for 75,000 h under the action of creep-carburization,meanwhile the damage value is only 0.53 along the outer surface after operating the same time under the action of creep alone,which means that microcracks are generated along the inner surface under the action of coupled creep-carburization,fracture begins along the outer surface of tube under the action of creep alone.

参考文献

[1] J. Klower;U. Heubner .Carburisation of nickel-base alloys and its effects on the mechanical properties[J].Materials and Corrosion,1998(4):237-245.
[2] X. Q. Wu;H. M. Jing;Y. G. Zheng;Z. M. Yao;W. Ke .Coking of HP tubes in ethylene steam cracking plant and its mitigation[J].British Corrosion Journal,2001(2):121-126.
[3] A. A. Kaya .Microstructure of HK40 alloy after high-temperature service in oxidizing/carburizing environment[J].Materials Characterization,2002(1):23-34.
[4] Y. Nishiyama;N. Otsuka;T. Nishizawa .Carburization Resistance of Austenitic Alloys in CH_4-CO_2-H_2 Gas Mixtures at Elevated Temperatures[J].Corrosion: The Journal of Science and Engineering,2003(8):688-700.
[5] T. H. Hyde;W. Sun;J. A. Williams .Life estimation of pressurised pipe bends using steady-state creep reference rupture stresses[J].International Journal of Pressure Vessels and Piping,2002(12):799-805.
[6] T.H. Hyde;A.A. Becker;W. Sun .Influence of geometry change on creep failure life of 90 deg pressurised pipe bends with no initial ovality[J].International Journal of Pressure Vessels and Piping,2005(7):509-516.
[7] J.M.Gong;S.T.Tu .Damage assessment and maintenance strategy of hydrogen reformer furnace tubes[J].Engineering failure analysis,1999(3):143-153.
[8] T. H. Hyde;W. Sun;J. A. Williams .Life estimation of pressurised pipe bends using steady-state creep reference rupture stresses[J].International Journal of Pressure Vessels and Piping,2002(12):799-805.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%