以Li3xLa0.67-xTiO3为母体,通过掺杂经高温固相反应制得了一系列新的锂快离子导体材料Li3xLa0.67-xInyTi1-2yNbyO3.利用X射线衍射分析和交流阻抗技术研究该系统的组成结构和电化学性能.结果表明体系合成温度降低,分解电压提高了;在x=0.10,y＜0.050时,合成物为单一的钙钛矿固溶体,y≥0.050时,则存在In2O3杂相;该体系合成物在室温下有较高的电导率,可达5.81×10-4S/cm,活化能在20～30kJ/mol之间.
参考文献
| [1] | Wang W J;Li D Y .[J].Celon J of Science,1995,2(01):26. |
| [2] | Wang WJ.;Liu XF. .STUDY ON SODIUM FAST ION CONDUCTORS IN THE NA1+3XALXHF2-XSI2XP3-2XO12 SYSTEM[J].Solid state ionics,1996(1/2):165-168. |
| [3] | Wang W J;Zhang Y R .[J].Solid State Ionics,1996,88:281. |
| [4] | Inaguma Y;Chen L;Itoh M et al.[J].Solid State Ionics,1994,70-71:196. |
| [5] | Bohnké O;Bohnké C;Fourquet J L et al.[J].Solid State Ionics,1996,91:21. |
| [6] | Katsumata T;Inaguma Y;Itoh M .[J].Solid State Ionics,1998,465:113. |
| [7] | Bonhké O;Emery J;Fourquet J L et al.[J].Solid State Ionics,1998,109:25. |
| [8] | Harada Y;Watanabe H;Kuwano J et al.[J].Journal of Power Sources,1999,81-82:777. |
| [9] | Harada Y.;Kawai H.;Kuwano J.;Ishigaki T. .Lithium ion conductivity of polycrystalline perovskite La0.67-xLi3xTiO3 with ordered and disordered arrangements of the A-site ions[J].Solid state ionics,1998(1/4):407-413. |
| [10] | Ivanov-Schitz A K;VKireev V;GChaban N .[J].Solid State Ionics,2000,136-137:407. |
| [11] | He L X;Yoo H I .[J].Electrochimica Acta,2003,48:1357. |
| [12] | Wen Z Y;Li J X;Xu X X et al.[J].Solid State Ionics,2005,176:2269. |
| [13] | 元素周期表[M].南京:南京大学化学系,1974 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%