在实验室条件下，系统研究了1380℃下，钒在FeO—SiO2一MnO渣系与铁液间的分配行为。结果表明：钒的提取率、钒在渣一金两相的分配比、渣的钒容量随渣中SiO2的质量分数升高而降低。在SiO2的质量分数较低时，以上参数随MnO质量分数的增加而升高。而在SiO2的质量分数较高（〉20％）时，随MnO质量分数的增加呈现先升高后降低的趋势。FeO-SiO2一MnO三元渣系中，siO2的质量分数为10％～20％、MnO的质量分数为13％～5％时，以上参数达到最大值，且该区域对应着FeO-SiO2一MnO渣系熔点最低的区域。V2O3在FeO-SiO2一MnO渣系中活度系数的数量级为10^-6～10^-7。
Under laboratory conditions, the distribution behavior of vanadium between hot metal and slag system of FeO-SiOz-MnO slag at 1 380 ℃ was studied. The results show： the extraction rate of vanadium {rom the hot metal, the distribution ratio of vanadium between slag and metal phases, and vanadium capacity of slag decrease with increasing SiO2 content; the parameters mentioned above increase with increasing MnO content in the condition of keeping SiOz content at lower level, when the SiOz content is larger than 20% they firstly increase and then decrease with increasing MnO content;in the slag system of FeO-SiOz-MnO, they reach the maximum value in the region of keeping w（SiOz ） at 10%0-20% and w（MnO） at 13%-25%, which is corresponding to the region of giving the lowest melting point; the magnitude of the activity coefficient of VzOa in FeO-SiO2-MnO slag system is 10^-6-10^-7.
参考文献
| [1] | 李远洲.底吹氧气转炉吹钒工艺的热力学分析之一[J].马鞍山钢铁学院学报,1984(01):12-22. |
| [2] | 张丙怀,李长伟,孙锦彪.CaO-SiO2-Al2O3-MgO-V2O5渣系熔融还原过程中钒的平衡分配[J].钢铁钒钛,1991(03):25. |
| [3] | 杨素波,罗泽中,蔡开科,姜钧普,宋波.钒在铁液和转炉渣间分配的热力学研究[J].钢铁,2006(03):36-38. |
| [4] | 刘天中,王大光,宣德茂.碳饱和铁水与CaO-SiO2-VxOy熔渣平衡体系间各组元的分配[J].钢铁钒钛,1991(04):1. |
| [5] | Ryo Inoue;Hideaki Suito .Distribution of Vanadium Between Liquid Iron and MgO Saturated Slags of the System CaO-MgO-FeOx-SiOz[J].Transactions of the Iron and Steel Institute of Japan,1982,22(09):705. |
| [6] | 李丹柯 .含钒铁水钒氧化动力学研究[D].重庆大学,2009. |
| [7] | Inoue R .Distribution of Vanadium Between Liquid Iron and MgO Saturated Slag[J].Transactions of the Iron and Steel Institute of Japan,1998,229(09):705. |
| [8] | 周建波;薛向欣;段培宁 .CaO-SiOz-Alz03-MgO-Vz05炉渣中非化学计量物VO:的热力学[J].中国有色金属学报,1998,8(z2):492. |
| [9] | Werme;Anders .Recovery of Vanadium from Hot Metal-Thermodynamics and Injection Applications[J].Scandinavian Journal of Metallurgy,1986,15(06):273. |
| [10] | 陈东辉;杨树德.钒渣化学形成理论研究[J].河北冶金,1993(05):32. |
| [11] | 黄希祜.钢铁冶金原理[M].北京:冶金工业出版社,2002 |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%