采用搅拌摩擦焊工艺对AZ80镁合金进行焊接,在其它工艺参数不变的条件下,研究了焊接速度对接头成形及组织的影响.结果表明:在搅拌头旋转速度为1 000 r· min-1、焊接速度为150 mm·min-1时可获得表面无缺陷、内部无孔洞的致密焊缝;焊速越大,焊核区前进侧中部组织中的动态再结晶晶粒越细小,焊速对热机影响区和热影响区组织的影响基本相同.
参考文献
[1] | 马春生,张治民,郭玉明.汽车镁合金轮毂等温挤旋成型工艺优化与试验[J].农业机械学报,2012(03):223-229. |
[2] | 杨素媛,张保垒.厚板AZ31镁合金搅拌摩擦焊焊接接头的组织与性能[J].焊接学报,2009(05):1-4. |
[3] | A. Forcellese;F. Gabrielli;M. Simoncini .Mechanical properties and microstructure of joints in AZ31 thin sheets obtained by friction stir welding using 'pin' and 'pinless' tool configurations[J].Materials & design,2012(Feb.):219-229. |
[4] | Afrin, N;Chen, DL;Cao, X;Jahazi, M .Microstructure and tensile properties of friction stir welded AZ31B magnesium alloy[J].Materials Science and Engineering. A, Structural Materials: Properties, Microstructure and Processing,2008(1/2):179-186. |
[5] | Yuan-Ching Lin;Ju-Jen Liu;Ben-Yuan Lin;Chun-Ming Lin;Hsien-Lung Tsai .Effects of process parameters on strength of Mg alloy AZ61 friction stir spot welds[J].Materials & design,2012(Mar.):350-357. |
[6] | A. RAZAL ROSE,K. MANISEKAR,V. BALASUBRAMANIAN.轴向力对搅拌摩擦焊接AZ61A镁合金拉伸性能的影响[J].中国有色金属学报(英文版),2011(05):974-984. |
[7] | 徐卫平,邢丽,柯黎明,孙德超.镁合金搅拌摩擦焊接头晶粒取向和织构分析[J].材料科学与工艺,2005(03):254-257. |
[8] | Duo Liu;Hiroyuki Nishio;Kazuhiro Nakata .Anisotropic property of material arrangement in friction stir welding of dissimilar Mg alloys[J].Materials & design,2011(10):4818-4824. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%