采用粉末注射成形工艺制备了无镍高氮奥氏体不锈钢(0Cr17Mn11Mo3N),研究了喂料的流变行为,注射工艺及烧结工艺.结果表明:64 vol%气雾化0Cr17Mn11Mo3粉末与适量的粘结剂(65 wt%石蜡+30 wt%高密度聚乙烯+5 wt%硬脂酸)混合后的喂料具有较好的流变性能;最佳注射工艺参数为注射压力75～95 MPa,相应的注射温度为160～170℃;提高烧结温度有利于提高烧结体的密度,但是对提高氮含量不利,而增加烧结氮气氛压力可以获得较高的氮含量,但是不利于提高烧结体密度,最佳的烧结工艺为0.1 MPa氮气压力下1300℃烧结2 h,此时烧结体相对密度町以达到99%,氮含量可达到0.78%.
参考文献
| [1] | Sumita M;Hanawa T;Teoh S H .Development of nitrogen-containing nickel-free austenitic stainless steels for metallic biomatarials-review[J].Materials Science and Engineering C,2004,24(6-8):753-760. |
| [2] | Yibin REN,Ke YANG,Bingchun ZHANG,Yaqing WANG,Yong LIANG.Nickel-free Stainless Steel for Medical Applications[J].材料科学技术学报（英文版）,2004(05):571-573. |
| [3] | Kelly Alvarez;Soong-Keun Hyun;Hiroaki Tsuchiya;Shinji Fujimoto;Hideo Nakajima .Corrosion behaviour of Lotus-type porous high nitrogen nickel-free stainless steels[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2008(1):183-193. |
| [4] | Simmons J W .Overview:high-nitrogen alloying of stainless steels[J].Materials Science and Engineering A,1996,207(02):159-169. |
| [5] | 周灿栋,丁伟中,蒋国昌.高氮钢的熔炼及试生产技术[J].包头钢铁学院学报,1999(Z1):387. |
| [6] | Y. Katada;M. Sagara;Y. Kobayashi .Fabrication of High Strength High Nitrogen Stainless Steel with Excellent Corrosion Resistance and Its Mechanical Properties[J].Materials and Manufacturing Processes,2004(1):19-30. |
| [7] | Ustinovshikov Y;Bannykh O;Blinov V;Kostina M;Ruts A .Microstructure and properties of the high-nitrogen Fe-Cr austenite[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1999(1/2):82-87. |
| [8] | German R M.Powder Injection Molding[M].Princeton:MPIF,1990 |
| [9] | 李笃信,黄伯云.金属注射成形技术的研究现状[J].材料科学与工程,2002(01):136-139. |
| [10] | 李益民,曲选辉,黄柏云.金属注射成形喂料的流动行为及粘度参数的测定[J].稀有金属材料与工程,1997(01):41-43. |
| [11] | J. -B. Vogt .Fatigue properties of high nitrogen steels[J].Journal of Materials Processing Technology,2001(3):364-369. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%