以武钢CSP工艺生产的DC04钢板作为冷轧基材,经冷轧后,在实验室模拟现场工艺进行了退火,利用光学显微镜和电子背散射衍射技术分析了退火过程中的组织和织构的演变.结果表明,DC04冷轧薄板在710℃退火3h后,再结晶基本完成,并且晶粒尺寸较均匀.在710℃退火时,随着退火时间的延长,小角度晶界所占比例逐渐减小,大角度晶界所占比例逐渐增大.在710℃退火12 h后,有较强的γ取向线和较弱的α取向线,即获得了理想的退火织构.
参考文献
| [1] | Gunter Flemming;Karl-Ernst Hensger .Present and future CSP technology expands product range[J].Iron & Steel Review,2000(1):53-57. |
| [2] | 康永林;傅杰;柳得橹.薄板坯连铸连轧钢的组织性能控制[M].北京:冶金工业出版社,2006 |
| [3] | 李一鸣,金自力,任慧平,王玉峰,田荣彬.CSP冷轧低碳钢板的再结晶织构[J].中国体视学与图像分析,2010(01):49-53. |
| [4] | Daniel D;Jonas J J .Measurement and prediction of plastic anisotropy in deep-drawing steels[J].Metall Mater Transact A,1990,21(01):331. |
| [5] | 毛卫民;赵新兵.金属的再结晶与晶粒长大[M].北京:冶金工业出版社,1994 |
| [6] | I. Samajdar .Development of recrystallization texture in IF-steel: an effort to explain developments in global texture from microtextural studies[J].Acta materialia,1998(8):2751-2763. |
| [7] | Hillert M .On the theory of normal and abnormal grain growth[J].Acta Metallurgica,1965,13:227. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%