通过有机物分解碳化处理TiO2 纳米管制得了TiO2C,并以其为载体制备了Pd/TiO2C电催化剂,考察了该催化剂对碱性介质中乙醇电催化氧化的活性. 结果表明,碳化导电处理的TiO2C纳米管载体能有效改善催化剂中贵金属的分散度和电极结构,从而提高催化剂的电催化活性. 对催化剂活性组分的优化实验表明,Pd/TiO2C质量比为1/1时催化剂的活性最高. 在1 mol/L KOH溶液中Pd载量均为0.3 mg/cm2的条件下,Pd/TiO2C催化剂对乙醇氧化的催化活性是Pd/C催化剂的3.8倍.
参考文献
| [1] | 范崇政,肖建平,丁延伟.纳米TiO2的制备与光催化反应研究进展[J].科学通报,2001(04):265-272. |
| [2] | Kang M .[J].Applied Catalysis B:Environmental,2002,37(03):187. |
| [3] | Fujishima F;Honda K .[J].Nature,1972,238(5358):37. |
| [4] | O'Regan B;Graetzel M .[J].Nature,1991,353(6346):737. |
| [5] | Sugimoto W;Iwata H;Yasunaga Y;Murakami Y,Takasu Y .[J].Angewandte Chemie International Edition,2003,42(34):4092. |
| [6] | Garcia, T;Solsona, B;Taylor, SH .The oxidative destruction of hydrocarbon volatile organic compounds using palladium-vanadia-titania catalysts[J].Catalysis Letters,2004(1/2):99-103. |
| [7] | Zhu H Q;Qin Z F;Shan W J;Shen W J Wang J G .[J].Journal of Catalysis,2004,225(02):267. |
| [8] | 佘沛亮,姚士冰,周绍民.电沉积制备钯铂电极上乙醇的电催化氧化[J].物理化学学报,2000(01):22-26. |
| [9] | 孙杰,吴锋,邱新平,王国庆,朱文涛,陈实,陈立泉.燃料电池的氢源技术--乙醇重整制氢研究进展[J].电源技术,2004(07):452-457. |
| [10] | Maggio G;Freni S;Cavallaro S .[J].Journal of Power Sources,1998,74(01):17. |
| [11] | Song SQ;Zhou WJ;Liang ZX;Cai R;Sun GQ;Xin Q;Stergiopoulos V;Tsiakaras P .The effect of methanol and ethanol cross-over on the performance of PtRu/C-based anode DAFCs[J].Applied Catalysis, B. Environmental: An International Journal Devoted to Catalytic Science and Its Applications,2005(1):65-72. |
| [12] | 姜鲁华,臧海霞,孙公权,辛勤.制备方法对直接乙醇燃料电池阳极PtSn/C催化剂性能的影响[J].催化学报,2006(01):15-19. |
| [13] | 赵新生,姜鲁华,孙公权,杨少华,衣宝廉,辛勤.新型Pt-Sn/C阳极催化剂对乙醇的电催化氧化性能[J].催化学报,2004(12):983-988. |
| [14] | Shen P K;Xu C W .[J].Electrochemistry Communications,2006,8:184. |
| [15] | Kasuga T.;Hoson A.;Sekino T.;Niihara K.;Hiramatsu M. .Formation of titanium oxide nanotube[J].Langmuir: The ACS Journal of Surfaces and Colloids,1998(12):3160-3163. |
| [16] | Seo DS.;Kim H.;Lee JK. .Preparation of nanotube-shaped TiO2 powder[J].Journal of Crystal Growth,2001(1):428-432. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%