以LiTi2(PO4)3为母体,天然高岭石为起始原料,经高温固相反应制得了一系列新的锂快离子导体材料Li1+2xA1xScyNbyTi2-x-2ySixP3-xO12(以下简称Sc-Nb-Lisicon).X射线衍射分析表明x=0.1、x=0.2,y≤0.4;x=0.3,y≤0.25的组成范围内能得到类似于Nasicon的三方结构,即空间点群为R3C的合成物.应用交流阻抗技术测试其电导率,结果表明:x=0.1,y=0.3及x=0.2,y=0.15的合成物在室温下有较高的电导率,分别为1.05×10-4S/cm和2.78×10-4S/cm,二者在573K时的电导率可达8.00×10-3S/cm和7.82×10-3S/cm,同时在423～573K具有较低的活化能,分别为31.4kJ/mol和34.8kJ/mol.
参考文献
| [1] | Robertson A D;Garcia Martin S;Coats A et al.[J].Journal of Materials Chemistry,1995,5(09):1405. |
| [2] | Bohnke C.;Fourquet JL.;Bohnke O. .ELECTROCHEMICAL INTERCALATION OF LITHIUM INTO LILANB2O7 PEROVSKITE[J].Journal of the Electrochemical Society,1997(4):1151-1158. |
| [3] | Bonhke O;Emery J;Fourquet J L et al.[J].Solid State Ionics,1998,109:25-34. |
| [4] | Harada Y;Watanabe H;Kuwano J.[J].Journal of Power Sources,1999:777-781. |
| [5] | Harada Y.;Kawai H.;Kuwano J.;Ishigaki T. .Lithium ion conductivity of polycrystalline perovskite La0.67-xLi3xTiO3 with ordered and disordered arrangements of the A-site ions[J].Solid state ionics,1998(1/4):407-413. |
| [6] | Wang Wenji;Li Duanyang .[J].Celon J of Science,1995,2(02):26. |
| [7] | Wang Wenji;Liu Xingfeng .[J].Solid State Ionics,1996,89:165-168. |
| [8] | Wang Wenji;Zhang Yurong .[J].Solid State Ionics,1996,88:281-284. |
| [9] | Wang Wenji;Wang Shifan.[A].广州,1996:370. |
| [10] | Wang Wenji;Wang Shifan.[A].,1996:330. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%