污损释放型防污漆用连接漆的应用研究

1.厦门双瑞船舶涂料有限公司,福建厦门361101

2.海洋腐蚀与防护重点实验室,福建厦门361101

3.海洋腐蚀与防护重点实验室,福建厦门361101

4.厦门双瑞船舶涂料有限公司,福建厦门361101

基金项目: 国防973项目(YK090901)

Research and Application of Tie-coatings For the Release Antifouling Paints

采用XPS、附着强度、耐海水浸泡等测试手段,研究了一种三组份有机硅环氧连接漆与防锈底漆和污损释放型防污漆界面化学键合强度.结果表明:有机硅环氧连接漆可以与防锈底漆发生界面化学键合,当附着促进剂添加量为6.0％时,与防污涂层连接效果最佳.

[1]	王胜龙,汤黎容,王晶晶,吴波.高连接强度改性丙烯酸酯连接漆的研究及应用[J].涂料工业,2013(12):6-9.
[2]	Jacob R.Svendsen;Georgios M.Kontogeorgis;Soren Kiil .Adhesion between coating layers based on epoxy and silicone[J].Journal of Colloid and Interface Science,2007(2):678-686.
[3]	Yebra DM;Kiil S;Dam-Johansen K .Antifouling technology - past, present and future steps towards efficient and environmentally friendly antifouling coatings[J].Progress in Organic Coatings: An International Review Journal,2004(2):75-104.
[4]	Robert M;Philip B N;John R .Segregating Coating Composition and Copolymer Therefor[P].WO 9426832,1994.
[5]	王胜龙,汤黎容,杨名亮,叶章基.丙烯酸/环氧树脂自分层的研究[J].材料开发与应用,2014(01):53-57.
[6]	任润桃,梁军.海洋防污涂料发展现状与研究趋势[J].材料开发与应用,2014(01):1-8.

上一张下一张

计量

作者相关

文章评分