Decopperization in molten steel with FeS-Na2 S slag was investigated in the laboratory. It was found that with an increase in FeS content of the FeS-Na2 S slag, the deeopperization ratio increased. The decopperization ratio could reach the maximum of 71.6% in hot metal. The decopperization ratio was closely related to the carbon con-tent, and the higher the carbon content, the higher was the decopperization ratio. Sulphur addition was found in the process of decopperization, and the increase in sulphur content of molten steel was about 0.2%-0.42%. However, by adding 30%-50% of BaO to the FeS-Na2 S slag, the addition of sulfur content in molten steel could be reduced by about 50%. The finer slag system composition was FeS:Na2S:BaO=40:20:40.
参考文献
| [1] | 钢液气化脱铜[J].北京科技大学学报,1999(02):161. |
| [2] | 李素芹,于秉杰,李士琦,李联生.熔体过滤法钢液脱铜技术探索[J].化工冶金,2000(03):314-317. |
| [3] | Wang C;Nagasaka T;Hino M et al.Copper Distribution Between Molten FeS-NaS0.5 Flux and Carbon Saturated Iron Melt[J].ISIJ International,1991,31(11):1300. |
| [4] | Wang C;Nagasaka T;Hino M et al.Copper Distribution Between FeS-Alkaline or Alkaline Earth Metal Sulfide Fluxes and Carbon Saturated Iron Melt[J].ISIJ International,1991,31(11):1309. |
| [5] | Imai T;Sano N .The Copper Partition Between Na2S Bearing Fluxes and Carbon-Saturated Iron Melt[J].Transactions of the Iron and Steel Institute of Japan,1988,28(12):999. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%