在测试了高硼高速钢轧辊材料临界点和等温转变曲线(TTT)的基础上,借助金相显微镜、扫描电镜、X衍射分析、拉伸试验、冲击试验和硬度试验等手段,研究了淬火处理对高硼高速钢轧辊材料组织与性能的影响.结果表明,高硼高速钢轧辊材料具有很好的淬透性,淬火后易获得高硬度的马氏体组织,且碳硼化合物呈孤立分布.淬火温度超过1050℃后,残留奥氏体增多,硬度反而下降.随着淬火温度升高,高硼高速钢的抗拉强度和冲击韧性提高,超过1050℃,抗拉强度的变化不明显.高硼高速钢在1050℃左右淬火,具有优良的综合性能.
参考文献
| [1] | Tomasz Babul;Zdzislaw Obuchowicz;Wiktor Grzelecki .Nitro-Oxidation of Tools Manufactured from High-Speed Steel[J].Materials and Manufacturing Processes,2009(7/9):842-846. |
| [2] | Akbari, A.;Mohammadzadeh, R.;Templier, C.;Riviere, J.P. .Effect of the initial microstructure on the plasma nitriding behavior of AISI M2 high speed steel[J].Surface & Coatings Technology,2010(24):4114-4120. |
| [3] | C. K. Kim;D.-G. Lee;S. Lee .Correlation of microstructure and fracture properties of five centrifugal cast high speed steel rolls[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2007(9):1065-1074. |
| [4] | N. F. Garza-Montes-de-Oca;W. M. Rainforth .Wear mechanisms experienced by a work roll grade high speed steel under different environmental conditions[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2009(Pt.1):441-448. |
| [5] | E. J. Kerr .High speed steel work rolls at dofasco[J].Iron & Steelmaker,2000(1):27-30. |
| [6] | Li J W;Zhang G S;Wei S Z et al.Preparation technology of the low carbon high boron Fe-C-B wear resistance steel[J].Applied Mechanics and Materials,2011,52-54:1718-1722. |
| [7] | 龚建勋,李丹,肖逸锋,张清辉.Fe-Cr-B-C堆焊合金的显微组织及耐磨性[J].材料热处理学报,2010(03):136-141. |
| [8] | H. Zhang;H. Fu;Y.Jiang;H. Cuo;Y. Lei;R. Zhou;Q. Cen .Effect of boron concentration on the solidification microstructure and properties of Fe-Cr-B alloy[J].Materialwissenschaft und Werkstofftechnik,2011(8):753-764. |
| [9] | H.-G. Fu;H.-J. Zhao;Z.-Z. Du .Heat treatment of centrifugally cast high carbon high vanadium high speed steel mill roll[J].Ironmaking & Steelmaking: Products and applications,2011(5):338-345. |
| [10] | 符寒光;邢建东.高速钢轧辊制造技术[M].北京:冶金工业出版社,2007 |
| [11] | 杜忠泽,符寒光,丰振军,李萍,戴建方.回火处理对铸造高速钢轧辊耐磨性的影响[J].材料热处理学报,2011(02):93-99. |
| [12] | Hoyle G.High Speed Steels[M].London:Butterworth & Co Ltd,1988:42-55. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%