对LaNixMn0.26A1y合金的储氢性能进行了研究.结果表明,与LaNi4.61Mn0.26Al0.13合金相比,LaNi4.5Mn0.26Al0.13合金的晶格常数和晶胞体积均变大,吸氢平台压力略有降低,放氢平台压力基本不变,滞后因子有所改善,储氢容量略有减少,氢化物生成焓绝对值变大,氢化物稳定性增加；对于LaNi4.4Mn0.26Al0.34合金,A1替代部分Ni使合金的晶格常数和晶胞体积变大,吸放氢平台压力明显降低,滞后因子明显改善,吸氢动力学性能显著提高,氢化物生成焓绝对值变大,氢化物更加稳定,但储氢容量有所减少.
参考文献
| [1] | 胡子龙.Hydrogen Storage Alloys(贮氢合金)[M].Beijing:Chemical Industrial Publishing Press,2002 |
| [2] | 张瑞静,吕曼祺,曹大力,陈德敏,杨柯.LaNi5-xAlx合金的Al含量对吸氢量和平衡氢压的影响[J].稀有金属,2004(04):678-682. |
| [3] | Cheng H H;Yang H G;Li S L et al.[J].Journal of Alloys and Compounds,2008,453:448. |
| [4] | Bonnet J E;Dantzer P;Dexpert H et al.[J].Journal of the Less-Common Metals,1987,130:491. |
| [5] | Nakamura H;Nakamura Y;Fujitani S et al.[J].Journal of Alloys and Compounds,1997,252:83. |
| [6] | 张瑞静,吕曼祺,陈德敏,杨柯.LaNi5-xMx（M=Al,Mn）合金的稳定性及储氢性能研究[J].金属学报,2005(04):427-432. |
| [7] | Lartigue C;Percheron-Guegan A;Achard J C et al.[J].Journal of the Less-Common Metals,1980,75:23. |
| [8] | Cheng H H;Deng X X;Li S L et al.[J].International Journal of Hydrogen Energy,2007,32:3046. |
| [9] | Okada M;Kuriiwa T;Tamura T et al.[J].Journal of Alloys and Compounds,1999,293-295:130. |
| [10] | Lundin C E;Lynch F E;Magee C B et al.[J].Journal of the Less-Common Metals,1977,56:19. |
| [11] | King H W .[J].Journal of Materials Science,1966,1:79. |
| [12] | Westlake D G .[J].Journal of the Less-Common Metals,1983,91:1. |
| [13] | 章应,罗永春,王大辉,张法亮,康家晨,闫如煦.AB2型LaMgNi3.7M0.3（M=Ni、Al、Mn、Co、Sn、Cu）贮氢合金的晶体结构及电极性能[J].功能材料,2005(09):1372-1376. |
| [14] | 谢昭明,付安庆,陈玉安,潘复生,丁培道.Al的添加对Mg2Ni储氢合金结构和氢扩散能力的影响研究[J].功能材料,2006(04):601-603. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%