In this paper,the microstructure of WC-Co alloys with and without nano-additives was characterized by scanning electron microscopy（SEM） and transmission electron microscopy（TEM）.The hardness and fracture toughness was tested by using a Vickers hardness tester and a universal testing machine.The cutting test was carried out at different feed velocities（250 r/min and 320 r/min）,and the contact pairs are cutting tools and 45# steel bars.Results showed that the hardness and fracture toughness of WC-Co cemented carbides with nano-additives are higher than that of WC-Co cemented carbides without nano-additives,and they are increased 10.21% and 19.69%,respectively.The flank worn width and crater width of cutting tools decrease greatly with the addition of nano-additives.For the nano-modified specimen with WC grain size of 7 μm,both the flank worn width and crater width are the minimum after the cutting process.And there are little built-up layers and some pile-up regions on the flank face leading to high cutting performance for the nano-modified cemented carbides.There are some melted regions on the flank face of cutting tools without nano-additives,and the WC grains on the cross section of alloys without nano-additives show severe fragmentation.The wear type of WC-Co is flank wear,and the wear mechanism is abrasive,adhesion and oxidation wear.
参考文献
| [1] | H. Juhr;H. -P. Schulze;G. Wollenberg .Improved cemented carbide properties after wire-EDM by pulse shaping[J].Journal of Materials Processing Technology,2004(1/3):178-183. |
| [2] | M. G. Gee;A. Gant;B. Roebuck .Wear mechanisms in abrasion and erosion of WC/Co and related hardmetals[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2007(1/6):137-148. |
| [3] | K. Bonny;P. De Baets;Y. Perez;J. Vleugels;B. Lauwers .Friction and wear characteristics of WC-Co cemented carbides in dry reciprocating sliding contact[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2010(11/12):1504-1517. |
| [4] | H. A. Abdel-Aal;M. Nouari;M. El Mansori .The effect of thermal property degradation on wear of WC-C0 inserts in dry cutting[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2008(11/12):1670-1679. |
| [5] | Z. N. Farhat .Microstructural characterization of WC-TiC-Co cutting tools during high-speed machining of P20 mold steel[J].Materials Characterization,2003(2/3):117-130. |
| [6] | C. Allen;M. Sheen;J. Williams;V. A. Pugsley .The wear of ultrafine WC-Co hard metals[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2001(1):604-610. |
| [7] | K. Bonny;P. De Baets;Y. Perez;J. Vleugels;B. Lauwers .Friction and wear characteristics of WC-Co cemented carbides in dry reciprocating sliding contact[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2010(11/12):1504-1517. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%