氢还原对钢材在大气腐蚀中的作用不可忽视,过去对其研究较少.采用电化学渗氢试验及慢应变速率拉伸方法研究了模拟海洋大气环境中SO<,2>浓度对16Mn钢应力腐蚀断裂及氢渗透行为的影响.结果表明,随着SO<,2>浓度的增大,试样断裂延伸率减小,断裂特征由塑性断裂逐渐转变为脆性断裂;随着SO<,2>浓度的增大,氢渗透电流增大,SO<,2>对氢渗透电流具有双重促进作用,第一个峰值的出现主要与SO<,2>的酸性有关,第二个峰值的出现主要是由于酸的再生循环所致.
参考文献
| [1] | Van Gelder K;Edings J G;Damen J W M et al.The stress corrosion cracking of duplex stainless steel in H《,2》 S/CO?《,2》/Cl《'-》 environments[J].Corms Science,1987,27(10,11):1271-1279. |
| [2] | Barteri M;Mancia F;Tamba A et al.Engineering diagrams and sulphide stress corrosion cracking of duplex stainless steels in deep sour well environment[J].Corms Science,1987,27(10,11):1239-1250. |
| [3] | Huang Y L;Zhu Y Y .Hydrogen ion reduction in the process of iron rusting[J].Corrosion Science,2005,47(06):1545-1554. |
| [4] | GJB 5877-2006.金属材料应力腐蚀开裂敏感性快速评价试验方法[S]. |
| [5] | Devnathan M A V;Stachurski Z .A technique for the evaluation of hydrogen embrittlement characteristics of electroplating baths[J].Journal of the Electrochemical Society,1963,110(08):886-894. |
| [6] | 张学元,柯克,杜元龙.金属在薄层液膜下电化学腐蚀电池的设计[J].中国腐蚀与防护学报,2001(02):117-122. |
| [7] | 陈惠玲,魏雨.碳钢在含SO2环境大气中腐蚀机理的研究[J].腐蚀与防护,2006(06):284-286. |
| [8] | 乔利杰;王燕斌;褚武扬.应力腐蚀机理[M].北京:科学出版社,1993:83. |
| [9] | Kobayashi M;Nishikata A;Tsuru T.Hydrogen embrittlement of reinforced steels in high alkaline chloride environments[A].山东青岛,2006:93-97. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%