研究TC4钛合金激光叠焊成形及焊缝显微组织特征,提出表征叠焊接头焊合程度的指标--焊合率ψ.研究结果表明:焊缝熔宽随着激光功率的升高和焊接速度的降低逐渐增加,上板焊缝熔宽大于下板焊缝,而连接焊缝处的熔宽最小;焊合率随着叠焊两板间间隙的增加或焊接线能量的升高而降低;焊缝组织为针状马氏体α'组成的"网篮"组织,上板焊缝中马氏体分布更密集;热影响区中存在少量细小马氏体组织,且呈梯度分布.由于马氏体的界面增强效应,使焊缝横向显微硬度沿焊缝中心向母材逐渐降低,且上板焊缝显微硬度略高于下板焊缝.
参考文献
| [1] | Han Wenbo;Zhang Kaifeng;Wang Guofeng .Superplastic forming and diffusion bonding for honeycomb structure of Ti-6Al-4V alloy[J].Journal of Materials Processing Technology,2007(2/3):450-454. |
| [2] | Wang S H;Wei M D;Tsay L W .[J].Materials Letters,2003,57(12):1818. |
| [3] | G. Casalino;F. Curcio;F. Memola Capece Minutolo .Investigation on Ti6Al4V laser welding using statistical and Taguchi approaches[J].Journal of Materials Processing Technology,2005(2/3):422-428. |
| [4] | Caiazzo F;Curcio F;Darrelio G et al.[J].Journal of Materials Processing Technology,2004,149(1-3):546. |
| [5] | Zhang Li;Gobbi S L;Norris I et al.[J].Journal of Materials Processing Technology,1997,65(1-3):203. |
| [6] | 吴会强,冯吉才,何景山,张秉刚.Ti-6Al-4V电子束焊接焊缝区域精细组织特征[J].航空材料学报,2005(03):21-24. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%