通过正交试验,研究了钝化电量、主盐浓度、钝化液pH与温度对甲磺酸盐镀锡板表面钝化膜铬含量、耐蚀性与漆膜结合力的影响。在本实验选定的参数范围内,钝化电量对以上3种性能都有较为显著的影响,尤其是漆膜结合力。钝化液pH对钝化膜的铬含量与耐蚀性影响最大,在实际生产中,钝化液的pH控制在4.2左右为最佳。生产高钝化电量镀锡板时,应避免采用过大的电流而影响钝化效果,并适当调低钢带走速作为配合。
The effects of the quantity of charge passed during passivation as well as the main salt concentration, pH, and temperature of passivation bath on chrome content and corrosion resistance of passivation film on surface of mesylate tinplate and on its adhesion to subsequent coating were studied. It was found that in range of the selected parameters, the quantity of charge has a remarkable effect on the properties especially coating adhesion of passivation film. The pH of passivation bath has the greatest influence on chrome content and corrosion resistance of passivation film. In practical production, the pH of passivation bath should be controlled at about 4.2. When passivating tinplate with high quantity of charge, the speed of steel strip movement should be appropriately reduced accordingly and the use of excessive current be avoided.
参考文献
[1] | 王晓东,黄久贵,李建中,田彦文,刘常升.国内外镀锡板生产发展状况[J].上海金属,2008(04):45-48. |
[2] | 林忠华.碱性镀锡的工艺维护与管理[J].电镀与精饰,1989(01):40. |
[3] | 肖鑫.高稳定性酸性光亮镀锡工艺研究[J].腐蚀与防护,2001(09):392-395. |
[4] | 章晓波.卤素法电镀锡板生产工艺的研究[J].有色冶金设计与研究,2005(02):4-7. |
[5] | 黄海泉;刘盛斌 .酸性镀锡液的新进展[J].电镀与涂饰,1994,13(03):51-53. |
[6] | 吴水清 .氨基磺酸盐在电镀工业中的应用[J].表面技术,1991,20(04):6-11. |
[7] | 叶晓燕,李立清.甲基磺酸盐电镀锡工艺及镀液性能[J].腐蚀与防护,2007(08):422-424. |
[8] | 王腾,安成强,郝建军.甲基磺酸盐镀锡添加剂研究进展[J].电镀与涂饰,2009(06):15-18. |
[9] | 王腾,孙丽芳,安成强.甲基磺酸盐电镀锡及锡合金的研究进展[J].电镀与精饰,2009(12):14-18. |
[10] | 谢龙,黄久贵,翟运飞,陈红星,黎德育,王志登,王洺浩,郑振,李宁.镀锡钢板表面钝化膜的形成机制[J].材料保护,2013(07):1-4. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%