研究了用涂敷法制备的碳纳米管(CNT)厚膜及其场发射特性,裂解法获得的碳纳米管与玻璃粉等混合、研磨,直接涂敷在Si基底上,经烧结后制成碳纳米管厚膜,二极结构测量的结果表明,碳纳米管厚膜有较低的开启电场(1.0～1.25V/μm),场强为5V/μm时,电流密度达到了50μA/cm2.该工艺的烧结过程应控制好,加热时间稍长会使CNT厚膜的场发射性能很快下降,时间过长会使CNT处在厚膜表面之下,无法有效发射电子.浆料中的玻璃粉比例增大时,碳纳米管阴极的场发射性能会有所降低.
参考文献
| [1] | Deheer WA;Chatelain A;Ugarte D .A CARBON NANOTUBE FIELD-EMISSION ELECTRON SOURCE[J].Science,1995(5239):1179-1180. |
| [2] | Saito Y.;Uemura S.;Uchida K.;Tasaka Y.;Ikazaki F. Yumura M.;Kasuya A.;Nishina Y.;Hamaguchi K. .Field emission from multi-walled carbon nanotubes and its application to electron tubes[J].Applied physics, A. Materials science & processing,1998(1):95-100. |
| [3] | Ajayan P M;Stephan O;Colliex C et al.[J].Science,1994,265(08):1212-1214. |
| [4] | Li W Z;Xie S S;Qian L X .[J].Science,1996,274(06):1701-1703. |
| [5] | Fan S S;Chapline M G;Franklin N R et al.[J].Science,1999,283(22):512-514. |
| [6] | Choi W B;Chung D S;Kang J H et al.[J].Applied Physics Letters,1999,75(20):3129-3131. |
| [7] | Kim J M;Choi W B;Lee N S et al.[J].Diamond and Related Materials,2000,9:1184-1189. |
| [8] | 刘卫华,朱长纯,王琪琨,李昕,皇甫鲁江.碳纳米管（CNT）场发射显示器的关键技术的研究[J].电子学报,2002(05):694-696. |
| [9] | Kwo J L;Yokoyama M;Wang W C et al.[J].Diamond and Related Materials,2000,9:1270-1274. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%