采用固相反应法合成了SrBi2Nb2O9,SrBi2.2Nb2O9,SrBi2.4Nb2O9,SrBi2.6Nb2O9(简称SBN系列)粉体,并用无压烧结方法制备出铁电陶瓷.通过扫描和透射电镜分析研究了材料的微观结构,利用阻抗分析仪测试了材料的介电性能和铁电性能,同时分析了不同配比对其组织性能的影响.研究发现,Bi含量不同,制备的陶瓷均为铋系层状类钙钛矿化合物,陶瓷的致密度约为95%.微观组织结构分析表明,晶粒形态均为层片状.SrBi2Nb2O9陶瓷的介电常数、介电损耗和剩余极化值分别为116μC/cm2,0.012μC/cm2,0.47μC/cm2.
参考文献
| [1] | Araujo C A;Cuchiare J D;Mcminan L D.[J].Nature,1995(374):627. |
| [2] | Dat R;Lee J K;Aucielli O.[J].Applied Physics Letters,1995(67):572. |
| [3] | Li T K;Zhu Y F;Desu S B.[J].Applied Physics Letters,1996(68):616. |
| [4] | Zhang ZG.;Wang YN.;Zhu JS.;Yan F.;Chen XB.;Shen HM.;Liu JS. .Fatigue characteristics of SrBi2Ta2O9 thin films prepared by metalorganic decomposition[J].Applied physics letters,1998(6):788-790. |
| [5] | Zhou Q F;Chan H L;Choy C L.[J].Journal of Non-Crystalline Solids,1999(254):106. |
| [6] | Ito Y;Ushikubo M;Yokoyama S.[J].Japanese Journal of Applied Physics,1996(35):4925. |
| [7] | Ravichandran D;Yamakawa K;Bhalla A S.[J].Journal of Sol-Gel Science and Technology,1997(09):95. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%