采用垂直布里奇曼法,生长出直径为30 mm的Hg3In2Te6晶体.通过透射电子显微镜观察Hg3In2Te6晶体和第二相粒子的形貌,并利用选区电子衍射技术分析其物相.结果表明:晶锭基体的物相为Hg0.5In0.33Te;同时观察到了HgTe、In2Te3等第二相,尺寸为10~40 nm.推测晶体发生分解是形成第二相的原因.
参考文献
[1] | Wang LH;Jie WQ .Single-crystal growth of mercury indium telluride (MIT) by vertical Bridgman method (VB)[J].Journal of Crystal Growth,2006(1):203-206. |
[2] | 张小雷,孙维国,鲁正雄,张亮,赵岚,丁嘉欣.Pt/Hg3In2Te6接触的温度特性研究[J].人工晶体学报,2009(04):888-892. |
[3] | 孙以材.半导体测试技术[M].北京:冶金工业出版社,1984:300. |
[4] | 王领航 .Hg(3-3x)In2xTe3晶体生长及性能表征[D].西安:西北工业大学,2008. |
[5] | Saunders G A;Seddon T .Effect of Ordered Vacancies on Ultrasonic Wave Propagation in Some Mercury-indium Tellurides[J].Physical and Chemistry of Solids,1970,31:2495-2504. |
[6] | Grushka O G;Grushka Z M;Frasunyak V M et al.Behavior of Manganese Impurities in Hg3In2Te6[J].Semiconductors (Translation of Fizika i Tekhnika Poluprovodnikov,1999,33(12):1272-1275. |
[7] | Leute V;Schmidtke H M .Thermodynamics and Kinetics of the Quasibinary System Hg(3-3x)In2xTe3.Investigations by X-ray Diffraction and Differential Thermoanalysis[J].Physical and Chemistry of Solids,1988,49(04):409-420. |