为研究大气污染物对镁合金腐蚀的影响规律,采用室内模拟暴露实验,分析AZ31镁合金含有NaCl和Na2SO4的薄层液膜下的电化学腐蚀行为.结果表明:AZ31镁合金表面沉积NaCl和Na2SO4薄液层中的腐蚀动力学符合幂函数规律,说明NaCl和Na2 SO4对AZ31镁合金腐蚀有加速作用;AZ31镁合金在NaCl薄层液膜下,阳极极化电流密度增大,Rf和Rct值降低,促进了阴极去极化历程,增强了阳极活性溶解,加剧镁合金的阳极溶解;而在Na2SO4薄层液膜下,Rf和Rct值增大,击穿电位与腐蚀电位的差值(△E)减小,这是由于难溶的硫酸盐和Mg(OH)2覆盖在AZ31镁合金表面,使金属溶解和离子扩散速率降低,导致阳极过程阻滞.
参考文献
| [1] | Influence of chloride ion concentration and temperature on the corrosion of Mg-Al alloys in salt fog[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2010(5):p.1696. |
| [2] | LIUWH;CAOF H;CHEN A et al.Corrosion behaviour of AM60 magnesium alloys containing Ce or La under thin electrolyte layers.Part 1:Microstructural characterization and electrochemical behaviour[J].Corrosion Science,2010,52(02):627-638. |
| [3] | LIN C;LI X G .Role of CO2 in the initial stage of atmospheric corrosion of AZ91 magnesium alloy in the presence of NaCI[J].Rare Matals,2005,25(02):190-196. |
| [4] | RAKEL L;LARS-GUNNAR J;GEORGE E T .Corrosion of magnesium in humid air[J].Corrosion Science,2004,46(05):1141-1158. |
| [5] | R. Arrabal;A. Pardo;M.C. Merino;M. Mohedano;P. Casajus;K. Paucar;G. Garces .Effect of Nd on the corrosion behaviour of AM50 and AZ91D magnesium alloys in 3.5 wt.% NaCl solution[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2012(Feb.):301-312. |
| [6] | Edward Ghali;Wolfgang Dietzel;Karl-Ulrich Kainer .Testing of General and Localized Corrosion of Magnesium Alloys: A Critical Review[J].Journal of Materials Engineering and Performance,2004(5):517-529. |
| [7] | ZENGRC;ZHANG J;HUANG W J et al.Review of studies on corrosion of magnesium alloys[J].Transactions of Nonferrous Metals Society of China,2006,16(02):763-771. |
| [8] | Ming-Chun Zhao;Patrik Schmutz;Samuel Brunner;Ming Liu;Guang-ling Song;Andrej Atrens .An exploratory study of the corrosion of Mg alloys during interrupted salt spray testing[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2009(6):1277-1292. |
| [9] | GUTMAN E M;UNIGOVSKI Y;ELIEZER A .Mechanoelectro chemical Behavior of Pure Magnesium and Magnesium Alloys Stressed in Aqueous Solutions[J].Journal of Materials Synthesis and Processing,2000,8(03):133-138. |
| [10] | H. Gao;Q. Li;F.N. Chen;Y. Dai;F. Luo;L.Q, Li .Study of the corrosion inhibition effect of sodium silicate on AZ91D magnesium alloy[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2011(4):1401-1407. |
| [11] | 王少楠,唐国翌,徐卓辉,信运昌,官磊.电轧AZ31镁合金在模拟海水中腐蚀行为研究[J].材料科学与工艺,2010(03):339-343. |
| [12] | M. Jamesh;Satendra Kumar;T.S.N. Sankara Narayanan .Corrosion behavior of commercially pure Mg and ZM21 Mg alloy in Ringer's solution - Long term evaluation by EIS[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2011(2):645-654. |
| [13] | Zhixia Qiao;Zhiming Shi;Norbert Hort;Nor Ishida Zainal Abidin;Andrej Atrens .Corrosion behaviour of a nominally high purity Mg ingot produced by permanent mould direct chill casting[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2012(Aug.):185-207. |
| [14] | 高声远,张志强,乐启炽,贾征,崔建忠.MgCO_3在AZ31镁合金中的细化效果及机理[J].材料科学与工艺,2011(03):49-52. |
| [15] | Xian-Fei Wang;Shou-Mei Xiong .Oxidation behavior of molten magnesium in atmospheres containing SO_2[J].Corrosion Science,2011(12):4050-4057. |
| [16] | LIU W J;CAO F H;JIAB L et al.Corrosionbehaviour of AM60 magnesiumalloys containing Ce or La under thinelectrolytelayers.Part 2:Corrosion product and characterization[J].Corrosion Science,2010,52(02):639-650. |
| [17] | Sannakaisa Virtanen .Biodegradable Mg and Mg alloys: Corrosion and biocompatibility[J].Materials Science & Engineering, B. Solid-State Materials for Advanced Technology,2011(20):1600-1608. |
| [18] | Hui Tang;Dezhen Yu;Yan Luo;Fuping Wang .Preparation and characterization of HA microflowers coating on AZ31 magnesium alloy by micro-arc oxidation and a solution treatment[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2013(Jan.1):816-822. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%