通过对AZ系镁合金钨极氩弧焊(TIG)焊接接头进行固溶时效处理,研究其显微组织和显微硬度的变化.结果表明,在时效初始阶段(0~10h),熔合区中Al和Zn元素扩散速度和β-Mg17(Al,Zn)12的体积分数增加较快,其显微硬度随之增加较快.随着时效时间的延长,熔合区中的βMg17(Al,Zn)12的析出逐渐达到饱和,β-Mg17(Al,Zn)12的体积分数不再增加,显微硬度基本不变.

参考文献

[1] Shen J;You G Q;Long S Y et al.[J].Materials Characterization,2008,59:1059-1065.
[2] Min M;Shen J;Lai S Q et al.[J].Materials Characterization,2009,60:1583-1590.
[3] Sun Z;Pan D .[J].Science and Technology of Welding & Joining,2002,7:343-351.
[4] Liu L M;Shen Y;Zhang Z D .[J].Science and Technology of Welding & Joining,2006,11:398-402.
[5] Wang XH;Wang KS .Microstructure and properties of friction stir butt-welded AZ31 magnesium alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2006(1-2):114-117.
[6] Munitz A;Cotler C;Stern A et al.[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2001,302:68-73.
[7] Cao X;Jahazi M;Immarigeon J P et al.[J].Journal of Materials Processing Technology,2006,171:188-204.
[8] Uematsu Y;Tokaji K;Matsumoto M .[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2009,517:138-145.
[9] González-Martinez R;Goken J;Letzig D et al.[J].Journal of Alloys and Compounds,2007,437:127-132.
[10] Zhu T P;Chen Z W;Gao W .[J].Materials Characterization,2008,59:1550-1558.
[11] Xu N;Shen J;Xie W D et al.[J].Materials Characterization,2010,61:713-719.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%