利用电镜、具备能谱分析功能的扫描电子显微镜和X射线衍射仪等分析设备,研究了一种新型Ni-Cr-W基高温合金Ni-20Cr-18W在1100℃的恒温氧化行为.通过试样的氧化增重,获得了氧化动力学规律.分析结果显示,在氧化初始阶段,合金表面生成了由六面体结构的Cr2O3,立方结构的NiO和与M3O4型氧化物同型的尖晶石结构(Ni,Mn,Cr)3O43种相组成的混合氧化膜.长时间氧化后,氧化膜由单层转变为双层,在内层形成连续的Cr2O3膜,在外层形成可以抑制内层Cr2O3挥发的致密NiO氧化膜；同时在氧化膜与合金基体界面处形成氧化孔洞,并且在该处发生A1元素的内氧化.
参考文献
| [1] | Caplan D;Cohen M .[J].Electrochemical Society,1961,108:438. |
| [2] | Berthod P .[J].Oxidation of Metals,2005,64:235. |
| [3] | Yoshiyuki Kaji;Hirokazu Tsuji;Hiroshi Nishi et al.[J].Journal of Nuclear Science and Technology,2002,39:928. |
| [4] | Dwaine L.Klarstrom .[P].United States Patent,No.4476091,1984. |
| [5] | Rikizo Watanabe;Yoshitaka Chiba .[P].United States Patent,No.4006015,1977. |
| [6] | Tatsuo Kondo;Hajime Nakijima;Masami Shindo .[P].United States Patent,No.5141704,1992. |
| [7] | Ju Choi;Chong K.Lee;Kyunggi-do .[P].United States Patent,No.4810466,1989. |
| [8] | Ju Choi;Hyon T Kim .[P].United States Patent,5419869,1995. |
| [9] | 唐增武,李金山,胡锐,刘毅,柏广海.固溶处理对Ni-Cr-W合金碳化物的影响[J].稀有金属材料与工程,2010(07):1157-1161. |
| [10] | Tang Zengwu;Li Jinshan;Hu Rui et al.[J].Materials Review,2010,24:48. |
| [11] | Berthod P;Aranda L;Podor R .[J].Oxidation of Metals,2005,63:57. |
| [12] | Litz J;Rahmel A;Schorr M .[J].Oxidation of Metals,1988,30:95. |
| [13] | Douglass D L .[J].Oxidation of Metals,1988,29:273. |
| [14] | Campbell C E;W J .[J].Acta Materialia,2002,50:77. |
| [15] | Stott F H;Wood G C;Stringert J .[J].Oxidation of Metals,1995,44:113. |
| [16] | 黄晓晓;李金山;胡锐 et al.[J].有金属材料与工程,2010,39(11):1908. |
| [17] | Espevik S;Rapp R A;Daniel P L et al.[J].Oxidation of Metals,1980,14:86. |
| [18] | Stott F H .[J].Materials Characterization,1992,28:311. |
| [19] | Tawancy H M .[J].Oxidation of Metals,1996,45:326. |
| [20] | SHIDA Y;Wood G C;Stott F H .[J].Corrosion Science,1981,21:581. |
| [21] | Stott F H;Wood G C;Shida Y et al.[J].Corrosion Science,1981,21:599. |
| [22] | U1-HamidA .[J].Oxidation of Metals,2002,57:217. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%