The symmetrical superlattice intrinsic stacking faults(SISFs)formed on {111} planes are the predominant crystal defects in polycrystalline Ni_3AI after slight deformation at room temper- ature.The formation of this kind of SISF is resulted from the dipoles which are distributed on the neighboring {111} planes after reorientation,dissociation and annihilation under applied stress.