Microstructure and hardness were investigated in pure Al samples with different purities (5N: 99.999%, 4N: 99.993%, and 2N: 99.7% in weight) subjected to dynamic plastic deformation at cryogenic temperatures. The saturated sizes of refined grains/subgrains in these samples induced by plastic deformation are about 240 nm without an obvious impurity effect, but the dislocation density in 2N Al is evidently higher than that in other samples. Boundary misorientations for 5N and 4N Al are below 10° with average values of 2–3°, while the average misorientation for 2N Al is obviously larger, being about 14°. Microhardness of LNT-DPD 2N Al is higher than that of 5N and 4N Al, owing to the enhanced dislocation density as their grain/subgrain sizes are almost identical.

参考文献

[1] P.W.J. Mckenzie;R. Lapovok;Y. Estrin .The influence of back pressure on ECAP processed AA 6016: Modeling and experiment[J].Acta materialia,2007(9):2985-2993.
[2] Y. M. Wang;M. W. Chen;H. W. Sheng .Nanocrystalline grain structures developed in commercial purity Cu by low-temperature cold rolling[J].Journal of Materials Research,2002(12):3004-3007.
[3] Y.S. Li;N.R. Tao;K. Lu .Microstructural evolution and nanostructure formation in copper during dynamic plastic deformation at cryogenic temperatures[J].Acta materialia,2008(2):230-241.
[4] C.Y. Yu;P.W. Kao;C.P. Chang .Transition of tensile deformation behaviors in ultrafine-grained aluminum[J].Acta materialia,2005(15):4019-4028.
[5] P. L. Sun;C. Y. Yu;P. W. Kao .Influence of Boundary Characters on the Tensile Behavior of Sub-Micron-Grained Aluminum[J].Scripta materialia,2005(4):265-269.
[6] F.Huang,N.R.Tao,K.Lu.Effects of Strain Rate and Deformation Temperature on Microstructures and Hardness in Plastically Deformed Pure Aluminum[J].材料科学技术学报(英文版),2011(01):1-7.
[7] Y.Iwahashi;Z.Horita;M.Nemoto .An investigation of microstructural evolution during equal-channel angular pressing[J].Acta materialia,1997(11):4733-4741.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%