为了提高汽车用热浸镀锌钢板的质量,防止泥浆附着腐蚀,延长其服役寿命,对镀锌钢板和基材进行了泥浆附着试验.采用SEM观察微观腐蚀形貌,以XRD分析产物成分,通过阻抗谱分析等技术研究了其腐蚀行为和腐蚀机理.结果表明:腐蚀初期,腐蚀速度逐渐加快,锈层厚度不断增大,锈层成分和厚度对镀锌钢板的腐蚀速度影响很大;镀锌钢板、基材的锈层电阻和电荷转移电阻都呈现先增后减的变化趋势;泥浆中的溶氧量和较高的Cl-含量对腐蚀速度都有很大的影响.
参考文献
| [1] | M. A. Arenas;J. de Damborenea .Use of electrochemical impedance spectroscopy to Study corrosion of galvanised steel in 0-6M NaCl solution[J].Corrosion Engineering, Science and Technology,2006(3):228-234. |
| [2] | Perez C;Collazo M;Izquierdo M et al.Comparative study between galvanized steel and three duplex systems submitted to a weathering cyclic test[J].Corrosion Science,2002,44(03):481-500. |
| [3] | D. A. Worsley;H. N. McMurray;J. H. Sullivan .Quantitative Assessment of Localized Corrosion Occurring on Galvanized Steel Samples Using the Scanning Vibrating Electrode Technique[J].Corrosion: The Journal of Science and Engineering,2004(5):437-447. |
| [4] | Barranco V;Feliu S;Feliu J S .EIS study of the corrosion behaviour of zinc-based coatings on steel in quiescent 3% NaCl solution.Part 1:directly exposed coatings[J].Corrosion Science,2004,46(09):2203-2220. |
| [5] | 王振尧,于国才,韩薇.3种有色金属在沈阳地区的大气腐蚀规律[J].中国有色金属学报,2003(02):367-372. |
| [6] | 章小鸽.锌和锌合金的腐蚀（二）[J].腐蚀与防护,2006(02):98-108. |
| [7] | 李谋成,林海潮,曹楚南.碳钢在土壤中腐蚀的电化学阻抗谱特征[J].中国腐蚀与防护学报,2000(02):111-117. |
| [8] | 王绍明,萧以德,张三平.SO2/盐雾复合循环加速腐蚀试验模拟锌在户外大气暴露腐蚀行为[J].腐蚀与防护,2005(01):13-17. |
| [9] | 王绍明,萧以德,张三平.锌及锌覆盖层户外大气暴露腐蚀行为的研究[J].材料保护,2004(11):24-26. |
| [10] | 董杰,董俊华,韩恩厚,刘春明,柯伟.低碳钢带锈电极的腐蚀行为[J].腐蚀科学与防护技术,2006(06):414-417. |
| [11] | 金名惠,孟厦兰,黄辉桃,杜桂焕.碳钢在我国四种土壤中腐蚀机理的研究[J].华中科技大学学报(自然科学版),2002(07):104-107. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%