Formation of Liquid Pools Entrapped within Solid Grains of ZA27 Alloys during Partial Remelting

材料科学技术（英文）, 2002, 18(6): 481-483.

^1, , ^2, , ^3,

1.State Key Laboratory of Mechanical Behavior for Materials, Xi'an Jiaotong University, Xi'an 710049, China;School of Materials Science and Engineering, Gansu University of Technology, Lanzhou 730050, China

2.School of Materials Science and Engineering, Gansu University of Technology, Lanzhou 730050, China

3.State Key Laboratory of Mechanical Behavior for Materials, Xi'an Jiaotong University, Xi'an 710049, China

基金项目: the Science and Technology Commission of Gansu Province, China(GS992-A52-024 and ZS011-A25-048-C)

Formation of Liquid Pools Entrapped within Solid Grains of ZA27 Alloys during Partial Remelting

Keywords： Thixoforming

The investigations were performed into the formation processes of liquid pools entrapped within solid grains of three ZA27 alloys, produced respectively by either grain refinement, or traditional permanent casting or mechanical stirring,during partial remelting at semisolid temperature of 460℃. The results show that the rapid coalescence of primary grains due to merging of secondary arms during the initial stage of partial remelting is the main cause for the formation of the entrapped liquid pools. This coalescence resulted in that a high quality of eutectics, especially the ηphase, was entrapped within the grains, and then remelted to form liquid pools during the subsequent heating. In addition, the growth of the ηphase decomposed from the primary α' phase and β phase and the subsequent remelting is another cause for the refined and permanent mould casting alloys. Furthermore, the agglomeration of the solid grains also resulted in the entrapment of liquid in the interior of grains.

参考文献

[1]	W R Loue;M Suery .[J].Materials Science and Engineering,1995,A203:1.
[2]	E Tzimas;A Zavaliangos .[J].Materials Science and Engineering,2000,A289:228.
[3]	E Tzimas;A Zavaliangos .[J].Materials Science and Engineering,2000,A289:217.
[4]	J. L. Wang;Y. H. Su;C. -Y. A. Tsao .STRUCTURAL EVOLUTION OF CONVENTIONAL CAST DENDRITIC AND SPRAY-CAST NON-DENDRITIC STRUCTURES DURING ISOTHERMAL HOLDING IN THE SEMI-SOLID STATE[J].Scripta materialia,1997(12):2003-2007.
[5]	J F Second;M Suery .[J].Journal of Materials Science,1984,19:3995.
[6]	T J Chen;Y Hao;J Sun.[J].Materials Science and Engineering,2002
[7]	Tijun CHEN;Ying MA;Yuan HAO;Song LU,Guangji XU and Jun SUN .[J].Trans. Nonferrous Metals Soc. China,2001,11(01):98.
[8]	Y S Yang;C -Y A Tsao .[J].Journal of Materials Science,1997,32:2087.
[9]	Du Zhi-ming,LUO Shou-jing,SUN Jia-kuan.Deformation mechanism of tension of 2024Al alloy at semi-solid state[J].中国有色金属学会会刊,2000(05):666.
[10]	M Durman;S Murphy .[J].Journal of Materials Science,1997,32:1603.
[11]	T Savaskan;S Murphy .[J].Materials Science and Technology,1990,6:695.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

Formation of Liquid Pools Entrapped within Solid Grains of ZA27 Alloys during Partial Remelting

参考文献