通过FT-IR仪,对制备的高岭土/NR/SBR/BR复合材料进行了系统的分析和研究.结果表明:硅烷偶联剂与高岭石表面产生了化学键合;在复合材料的硫化过程中硫磺与橡胶大分子形成了C-Sx-C键;高岭土的加入能够影响C-Sx-C键的形成,其内羟基能与橡胶大分子反应;高岭土在偶联剂的作用下融入橡胶基体中,提升了硫化胶的力学性能;FT-IR可以研究高岭土补强NR/SBR/BR复合材料的机理.
参考文献
| [1] | 夏光华,李晓鸣,赵晓东.北海高岭土矿物特征及铁赋存状态的研究[J].硅酸盐通报,2013(02):289-293. |
| [2] | 陈南春,龙飞,周友胜,胡如海.广西田阳高岭土精细化研究[J].硅酸盐通报,2004(04):47-50. |
| [3] | Rattanasom, N;Prasertsri, S .Relationship among mechanical properties, heat ageing resistance, cut growth behaviour and morphology in natural rubber: Partial replacement of clay with various types of carbon black at similar hardness level[J].Polymer Testing,2009(3):270-276. |
| [4] | 肖曲,管俊芳,高惠民,余俊,王国斌.宜昌煤系高岭土补强天然橡胶试验研究[J].矿产综合利用,2009(04):20-23. |
| [5] | 孙秀霞.傅里叶变换红外光谱法测定丁基橡胶的不饱和度[J].石化技术,2011(03):15-17. |
| [6] | Frost RL.;Mako E.;Kristof J.;Kloprogge JT. .Modification of kaolinite surfaces through mechanochemical treatment - a mid-IR and near-IR spectroscopic study[J].Spectrochimica acta, Part A. Molecular and biomolecular spectroscopy,2002(13):2849-2859. |
| [7] | 胡萍,姜明,黄畴,于谦.硅烷偶联剂的界面性能研究[J].表面技术,2004(05):19-21. |
| [8] | 陆银平,刘钦甫,牛胜元,李靖如.硅烷偶联剂改性纳米高岭土的研究[J].非金属矿,2008(05):9-11. |
| [9] | 杨慧群 .高岭土/白炭黑补强BR/SBR的试验研究[D].武汉理工大学,2012. |
| [10] | 吴静,陈玲,杨青,卢咏来,张立群.通用橡胶材料红外光谱分析（一）[J].中国橡胶,2012(04):46-48. |
| [11] | 张旺驰,胡明安,李金发,张利国.宜昌高岭土粉体表面改性红外光谱分析与机理研究[J].中国矿业,2006(01):45-47. |
| [12] | 徐廷婧,王河锦.景德镇地区高岭石红外光谱分析[J].岩石矿物学杂志,2010(01):59-66. |
| [13] | 何佳杰,向贤伟.丙烯酸类单体接枝改性氯化聚丙烯乳液的制备[J].合成树脂及塑料,2012(05):43-46. |
| [14] | 陈旭辉.天然橡胶与合成聚异戊二烯橡胶的红外光谱鉴定[J].光谱实验室,2001(03):314-316. |
| [15] | 杨春亮,钱红莲,王平粤.环氧化天然橡胶的硫化动力学分析[J].热带作物学报,2005(01):16-19. |
| [16] | 磺化聚苯乙烯胶体晶的红外光谱分析[J].高分子学报,2001(05):561-564. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%