用双螺杆挤出机制备了聚乳酸（PLA）、聚烯烃弹性体（POE）和4种不同增容剂（马来酸酐接枝POE、马来酸酐、丙烯酸酯双官能化POE、丙烯酸酯与缩水甘油酯双官能化的POE、甲基丙烯酸缩水甘油酯接枝POE）的共混物,考察了不同增容剂对共混物力学性能和断面形貌的影响,分析了退火前后共混物力学性能的变化。结果表明,在使用自制的甲基丙烯酸缩水甘油酯接枝POE（POE-g-GMA）作为增容剂,三元体系PLA/POE/POE-g-GMA的质量比为80/15/5时,复合材料力学性能达到最佳,此时缺口冲击强度为12.3 kJ/m2,是纯PLA的3.7倍,拉伸强度为47.5 MPa。
Poly（l-lactic acid）（PLA）,polyolefin elastomer（POE） and various compatibilizers blends were prepared via melt blending by means of twin-screw extruder.The influence of different compatibilizers on the mechanical property of the composites was investigated.The micromorphology of the PLA /POE composites containing different compatibilizers was measured by scanning electron microscopy（SEM）,and the influence of annealing on the mechanical property of the composites was also studied.The results indicate that POE-g-GMA,a self-made reactive compatibilizer is the best,and the mechanical property of the composite reaches optimum when the mass ratio of PLA,POE and POE-g-GMA is 80∶15∶5.Its tensile strength is 47.5MPa and Izod impact strength is 12.3 kJ/m2,which is 3.7 times as much as that of pure PLA.
参考文献
| [1] | Ho CH;Wang CH;Lin CI;Lee YD .Synthesis and characterization of TPO-PLA copolymer and its behavior as compatibilizer for PLA/TPO blends[J].Polymer: The International Journal for the Science and Technology of Polymers,2008(18):3902-3910. |
| [2] | 陈卫丰,居学成,翟茂林.完全生物降解聚乳酸共混复合材料的研究进展[J].高分子材料科学与工程,2011(02):171-174. |
| [3] | Anderson KS;Schreck KM;Hillmyer MA .Toughening polylactide[J].Polymer reviews,2008(1):85-108. |
| [4] | Lee CM;Kim ES;Yoon JS .Reactive blending of poly(L-lactic acid) with poly(ethylene-co-vinyl alcohol)[J].Journal of Applied Polymer Science,2005(2):886-890. |
| [5] | Su, ZZ;Li, QY;Liu, YJ;Hu, GH;Wu, CF .Compatibility and phase structure of binary blends of poly(lactic acid) and glycidyl methacrylate grafted poly(ethylene octane)[J].European Polymer Journal,2009(8):2428-2433. |
| [6] | Cartier H.;Hu GH. .Styrene-assisted free radical grafting of glycidyl methacrylate onto polyethylene in the melt[J].Journal of Polymer Science, Part A. Polymer Chemistry,1998(15):2763-2774. |
| [7] | Hu Guo-Hua;Cartier Herve .Styrene-Assisted Melt Free Radical Grafting of Glycidyl Methacrylate onto an Ethylene and Propylene Rubber[J].Journal of Applied Polymer Science,1999(1):125-133. |
| [8] | 李冰,董蓉,高磊,杨俊,施庆峰,郭卫红.聚乳酸木塑复合材料的增韧及结晶性能[J].高分子材料科学与工程,2011(02):33-36. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%