The hot deformation of an Al-Cu-Mg alloy was studied in the two temperature ranges (room temperature-300℃ and 400℃-480℃). The rate-independent flow curves are typical of elasto-plastic response with significant work hardening followed by strain softening below 300℃. Similar dislocation structures with high density tangled into grain interiors were observed by TEM, which suggests that the process of obstacles arresting mobile dislocations results in this macroscopically rate-independence. At 400-480℃, all rate dependent flow behaviors characterized by a continuous softening after an initial work hardening at a small plastic strain show large tensile elongations.Long dislocation segments around the second phases infer their good mobility to climb across obstacles. Grain boundary morphology observed by TEM suggests that the capacity of the grain boundaries to absorb the dislocations sensitively accounts for the rate-dependent mechanical properties.
参考文献
| [1] | S. Barbagallo;P. Cavaliere;E. Cerri .Compressive plastic deformation of an AS21X magnesium alloy produced by high pressure die casting at elevated temperatures[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):9-16. |
| [2] | A Majorell;S Srivatsa;R C Picu .[J].Materials Science and Engineering A,2002,326:297. |
| [3] | A K Ghosh .[J].Acta Materialia,1977,25:1413. |
| [4] | E W Hart .[J].Acta Materialia,1967,15:351. |
| [5] | W Y Kim;S Hanada .[J].Journal of Alloys and Compounds,2002,347:219. |
| [6] | A K Ghosh .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1982,13:733. |
| [7] | H Watanabe;H Tsutsui;T Mukai et al.[J].International Journal of Plasticity,2001,17:387. |
| [8] | D.M.Li;A. Ghosh .[J].Materials Science and Engineering A,2003,352:79. |
| [9] | R. Kaibyshev;T. Sakai;F. Musin .Superplastic behavior of a 7055 aluminum alloy[J].Scripta materialia,2001(12):1373-1380. |
| [10] | L.M. Dougherty;I.M. Robertson;J.S. Vetrano .Direct observation of the behavior of grain boundaries during continuous dynamic recrystallization in an Al-4Mg-O.3Sc alloy[J].Acta materialia,2003(15):4367-4378. |
| [11] | A Kaibyshev.Superplasticity of Alloy, Intermetallides and Ceramics(M)[M].springer-verlag, New York,1992:70. |
| [12] | T G Langdon .[J].Materials Science and Engineering A,1993,166:67. |
| [13] | R C Gifkins .[J].Materials Characterization,1994,32:59. |
| [14] | Y. TAKAYAMA;T. TOZAWA;H. KATO .SUPERPLASTICITY AND THICKNESS OF LIQUID PHASE IN THE VICINITY OF SOLIDUS TEMPERATURE IN A 7475 ALUMINUM ALLOY[J].Acta materialia,1999(4):1263-1270. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%