对铝含量为2％和4％(质量分数)的热轧态310S耐热钢进行不同条件下的固溶处理,用光学显微镜观察了显微组织,用EPMA-1600电子探针分析了组织中各元素分布,并进行了室温拉伸性能测试.结果表明,高铝310S耐热钢在1150 ℃固溶处理时,随着时间延长晶粒尺寸明显增大,Cr7C3颗粒和Al4C3颗粒含量均大幅度减少,残余的Cr7C3颗粒逐渐聚集长大,并和Al4C3颗粒一起沿晶界呈链条状析出;经1200℃×2h固溶处理,Cr7C3颗粒完全消失,而Al4C3相少量残余.高铝310S耐热钢合理的固溶处理工艺为:1200℃保温2h,然后水淬处理,经此工艺处理的试样抗拉强度和屈服强度均高于传统工艺(1150℃×30 min).
参考文献
| [1] | Y. YAMAMOTO;M.P. BRADY;M.L. SANTELLA .Overview of Strategies for High-Temperature Creep and Oxidation Resistance of Alumina-Forming Austenitic Stainless Steels[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2011(4):922-931. |
| [2] | 喇培清,刘辉,刘致远,王维国,魏玉鹏,卢学峰.Al对HP40合金高温力学性能的影响[J].兰州理工大学学报,2012(04):10-14. |
| [3] | Z.K. Teng;C.T. Liu;G. Ghosh;P.K. Liaw;M.E. Fine .Effects of Al on the microstructure and ductility of NiAl-strengthened ferritic steels at room temperature[J].Intermetallics,2010(8):1437-1443. |
| [4] | Xiangqi Xu;Xiaofeng Zhang;Guoliang Chen;Zhaoping Lu .Improvement of high-temperature oxidation resistance and strength in alumina-forming austenitic stainless steels[J].Materials Letters,2011(21/22):3285-3288. |
| [5] | 喇培清,李玉峰,刘闪光.铝对310S耐热钢高温抗氧化性能的影响研究[J].钢铁,2011(01):66-69. |
| [6] | 喇培清;刘闪光.Al元素对310S耐热钢组织和力学性能的影响研究[J].材料工程,2009(增刊1):36-40. |
| [7] | 喇培清,王鸿鼎,刘闪光,申达,刘雪梅,鞠倩.Al元素对310S耐热钢高温压缩性能的影响[J].兰州理工大学学报,2010(06):9-12. |
| [8] | 顾学民.铍、碱土金属、硼、Al、镓分族[M].北京:科学出版社,1990 |
| [9] | 侯东坡,宋仁伯,项建英,陈舒阳,任培东.固溶处理对316L不锈钢组织和性能的影响[J].材料热处理学报,2010(12):61-65. |
| [10] | 薛忍让,宋志刚,郑文杰,杜忠泽.固溶温度对316LN不锈钢组织及力学性能的影响[J].金属热处理,2013(04):88-91. |
| [11] | 喇培清,刘辉,孟倩,魏玉鹏.不同Al含量的310S耐热钢热轧加工后的组织和力学性能[J].兰州理工大学学报,2012(05):15-20. |
| [12] | 世界钢合金技术条件与牌号对照手册[S].北京:中国标准出版社,2005. |
| [13] | 卢星星,余际星,倪晓臣,程远存.固溶处理对0Cr16Ni16钢形变热处理后力学性能的影响[J].热处理技术与装备,2010(01):20-22. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%