以硝酸镍为原料,尿素为沉淀剂,在不添加任何模板和表面活性剂条件下,采用均匀沉淀法制备出具有自组装结构的花状α型Ni（OH）2,并以其为前驱体,制得了同样具有花状结构的NiO。采用XRD、SEM、HRTEM、TG和低温液氮吸附技术对样品的晶相结构、表面形貌和孔径结构等进行表征。测试结果显示,所制备的样品是α型Ni（OH）2,比表面积是245.0m2/g,而且这些直径为4～6μm的花状Ni（OH）2是由许多纳米薄片相互组装而成。将花状Ni（OH）2在400℃焙烧2h即可获得具有花状结构的NiO,其比表面积为125.2m2/g。
α-nickel hydroxide（Ni（OH）2） with flowerlike hierarchical architectures was successfully synthesized,using urea and Ni（NO3）2 as the starting materials.The prepared products were characterized by X-ray powder diffraction（XRD）,high-resolution transmission electron microscopy（HRTEM）,thermogravimetric analysis（TG） and N2 adsorption-desorption.According the results,the prepared Ni（OH）2 was typical α-phase with specific surface area of 245.0m2/g and showed flowerlike structure with 4-6μm in diameter.Flowerlike nickel oxide（NiO） with the similar flowerlike and the specific surface area of NiO was 125.2m2/g.
参考文献
| [1] | Hu WK.;Noreus D. .Alpha nickel hydroxides as lightweight nickel electrode materials for alkaline rechargeable cells[J].Chemistry of Materials,2003(4):974-978. |
| [2] | Liu HB;Xiang L;Jin Y .Hydrothermal modification and characterization of Ni(OH)(2) with high discharge capability[J].Crystal growth & design,2006(1):283-286. |
| [3] | 韦斐,吴也凡,罗凌虹,石纪军,程亮,苗立峰.花状NiO纳米片自组装体的制备与表征[J].硅酸盐学报,2009(12):1975-1981. |
| [4] | Cao MH;He XY;Chen J;Hu CW .Self-assembled nickel hydroxide three-dimensional nanostructures: A nanomaterial for alkaline rechargeable batteries[J].Crystal growth & design,2007(1):170-174. |
| [5] | 朱振峰,魏娜,刘辉,何作利,杨冬.自组装花状结构Ni（OH）2的微波水热合成与表征[J].功能材料,2011(03):436-440. |
| [6] | 孙海峰,蒋文全,于丽敏,傅钟臻.水热法合成纳米花瓣状β-Ni（OH）2[J].稀有金属,2010(03):389-394. |
| [7] | 彭美勋,王零森,沈湘黔,危亚辉,贺万宁.β-球形氢氧化镍的微观结构及其形成机理[J].中国有色金属学报,2003(05):1130-1135. |
| [8] | Chen XY;Zhang ZJ;Qiu ZG;Shi CW;Li XL .A facile biomolecule-assisted approach for fabricating alpha-Fe2O3 nanowires in solution[J].Solid State Communications,2006(6):267-269. |
| [9] | Chen JD;Wang YJ;Wei K;Zhang SH;Shi XT .Self-organization of hydroxyapatite nanorods through oriented attachment[J].Biomaterials,2007(14):2275-2280. |
| [10] | Yang M;Pang GS;Li JX;Jiang LF;Feng SH .Preparation of ZnO nanowires in a neutral aqueous system: Concentration effect on the orientation attachment process[J].European journal of inorganic chemistry,2006(19):3818-3822. |
| [11] | 邢伟,李丽,阎子峰,LU Gao-Qing.介孔氧化镍的合成、表征和在电化学电容器中的应用[J].化学学报,2005(19):1775-1781. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%