利用无水溶胶-凝胶技术制备了Ba0.7Sr0.3TiO3薄膜,采用TG-DSC对干凝胶的热反应过程进行了详细分析,结果表明,经过350℃和450℃处理后的非晶薄膜为碳酸盐而非钛酸盐.450℃退火1h处理的非晶薄膜在350～1000nm的光学透过率大于80％,在470nm处的折射率最大(1.94),消光系数较小(0.003).800℃退火1h获得了晶态薄膜,该晶态薄膜的光学透过率也较好,在λ=670nm处的折射率最大(2.05),消光系数为0.07.
参考文献
| [1] | Jia Qunping;Shen Bo;Hao Xihong et al.Enhanced dielectric property from highly (100)-oriented barium zirconate titanate compositional gradient films[J].Thin Solid Films,2010,518(24):e89. |
| [2] | Yun Ye;Tailiang Guo .Dielectric properties of Fe-doped Ba_(0.65)Sr_(0.35)TiO_3 thin films fabricated by the sol-gel method[J].CERAMICS INTERNATIONAL,2009(7):2761-2765. |
| [3] | 赵丽丽;吴淑荣;熊为淼 .高性能PTCR陶瓷材料的制备[J].西北大学学报(自然科学版),1999,29(06):528. |
| [4] | 赵丽丽,畅柱国,杨孟林,吴淑荣,熊为淼.改性剂Sb对BaTiO3基PTCR陶瓷电学性能的影响[J].西北大学学报(自然科学版),2001(05):406-408. |
| [5] | Wang D Y;Li S;Chan H L W et al.Electro-optic characterization of epitaxial Ba0.7Sr0.3TiO3 thin films using prism coupling technique[J].Current Applied Physics,2011,11(03):552. |
| [6] | 彭静,徐智谋,陈存华,揭泉林.（Ba0.8Sr0.2）TiO3薄膜的室温发光行为研究[J].华中科技大学学报（自然科学版）,2009(06):121-124. |
| [7] | 汪竞阳,章天金,江娟,潘瑞琨,詹芬.稀土Nd掺杂Ba0.65Sr0.35TiO3薄膜的微结构与光致发光性能研究[J].功能材料,2009(02):194-196,200. |
| [8] | 吴淑荣;李东升;赵丽丽.热分析在溶胶-凝胶制备PTCR BaTiO3基陶瓷过程中的应用[J].现代科学仪器,1998(05):51. |
| [9] | 张五星,徐重阳,王长安,赵伯芳.溶胶-凝胶法制备钛酸锶钡薄膜[J].压电与声光,2003(01):58-60. |
| [10] | 王龙德,崔鹏.溶胶-凝胶法制备（Ba0.7Sr0.25Cd0.05）TiO3纳米粉体[J].山东理工大学学报（自然科学版）,2010(03):33-36. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%