以金尾矿为主要原料,采用熔融法制备CaO-Al2O3-SiO2系微晶玻璃.利用差热分析(DSC)、X射线衍射分析(XRD)、扫描电镜(SEM)等分析手段对所制备的微晶玻璃进行了分析测试与表征,并研究了不同晶化温度对制得微晶玻璃的物相组成、微观结构及性能的影响.结果表明:在850～ 950℃下,随着晶化温度的提高,所制备微晶玻璃的性能均提高.确定较佳的晶化制度为950℃保温3h,所制备微晶玻璃的热膨胀系数、抗折强度及密度分别为68.7×10-7/℃,122 MPa和2.836 g/cm3.
参考文献
| [1] | 赖才书,胡显智,字富庭.我国矿山尾矿资源综合利用现状及对策[J].矿产综合利用,2011(04):11-14. |
| [2] | 曹耀华,刘红召,高照国.用灵湖金尾矿制取微晶玻璃的试验研究[J].金属矿山,2008(08):137-141. |
| [3] | 陈平.汉阴黄金尾矿综合利用途径探讨[J].金属矿山,2012(08):160-163. |
| [4] | Khater, G.A.;Abdel-Motelib, A.;El Manawi, A.W.;Abu Safiah, M.O. .Glass-ceramics materials from basaltic rocks and some industrial waste[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2012(8):1128-1134. |
| [5] | Khater, G.A. .Glass-ceramics in the CaO-MgO-Al2O3-SiO2 system based on industrial waste materials[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2011(52/54):3066-3070. |
| [6] | 王浩,陆雷,武相萍,隋普辉.烧结法制备锂锌硅微晶玻璃热处理制度的研究[J].人工晶体学报,2008(03):639-643. |
| [7] | 李保卫,邓磊波,张雪峰,贾晓林,赵鸣,张明星.矿渣微晶玻璃热处理制度的优化设计[J].硅酸盐通报,2012(06):1549-1553,1558. |
| [8] | 张大勇,史培阳,姜茂发.转炉渣微晶玻璃热处理制度研究[J].硅酸盐通报,2008(06):1096-1099. |
| [9] | Soon-Do Yoon,Jong-Un Lee,Jeong-Hwan Lee,Yeon-Hum Yun,Wang-Jung Yoon.Characterization of Wollastonite Glass-ceramics Made from Waste Glass and Coal Fly Ash[J].材料科学技术学报（英文版）,2013(02):149-153. |
| [10] | 张乐军,陆雷,王浩,赵莹.微晶玻璃烧结过程中晶化和致密化的关系[J].硅酸盐通报,2007(04):804-807,833. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%