利用差热分析、X射线衍射仪、液氮吸附BET孔经测试仪对组成为NaTi2(PO4)3-0.9 Ca3(PO4)2的含钛磷酸盐玻璃的析晶行为进行了研究.通过对该玻璃相继进行成核、析晶和酸浸泡处理制备了NaTi2(PO4)3骨架多孔微晶玻璃.证明该玻璃在646℃8h成核处理过程中产生了旋节分解特征的成分偏聚,形成了富TiO2玻璃相和富CaO玻璃相交错生长的连通结构,成核处理后的玻璃在738℃析晶过程中依次在富钛相和富钙相中析出NaTi2(PO4)3和β-Ca3(PO4)2.成核过程对析晶的促进作用是通过促进NaTi2(PO4)3的析出而实现的.
参考文献
| [1] | 张彪 .结构功能材料的性能[J].无机材料学报,1996,11(01):9-18. |
| [2] | Abe Y;Zhang Z;Hosono H .Porous glass-ceramics in the CaO-TiO2-P2O5 system[J].Journal of the American Ceramic Society,1989,72(09):1587-90. |
| [3] | Hosono H;Abe Y .Porous NaTi2 (PO4) 3 glass-ceramics[J].Journal of the Electrochemical Society,1990,137(10):3149-51. |
| [4] | Yamamoto K.;Abe Y. .Microporous glass-ceramics in NASICON-type copper(II) titanium phosphate[J].Journal of the American Ceramic Society,1998(8):2201-2204. |
| [5] | Simmons H;Uhlmann D R;Beall G H.Nucleation and crystallization in glass[M].The American Ceramic Society Inc,1982:275-79. |
| [6] | 袁彪;陈全庆 .用差热分析确定核化温度范围及动力学参数的的方法[J].玻璃与搪瓷,1989,18(06):41-44. |
| [7] | 西北轻工业学院.玻璃工艺学[M].北京:中国轻工业出版社,1997:45-62. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%