Nb/Nb5Si3 in-situ composites are very attractive structural materials because these materials perform a good balance in mechanical properties, including high strength at high temperature (＞ 1000℃) and reasonably high fracture toughness at room temperature. Metastable phase Nb3Si plays an important role in the properties of Nb/Nb5Si3 composites by affecting the volume fraction of ductile phase. The addition of Mo affects on the microstructure of ductile phase and the stability of metastable phase Nb3Si. In this paper, Nb-10Si-xMo and Nb-18Si-xMo (x = 0, 5, and 15) alloys were prepared by arc melting and annealed at 1473 K for 100 h. Single edge-notched bending (SENB) test was used to study the fracture toughness of Nb-Si-Mo alloys. The room temperature fracture toughness of Nb- 10Si is 10.48 MPa. m1/2 and higher than that of binary Nb- 18Si alloys at near-eutectic composites. The addition of 5 at.% Mo improved the fracture toughness of as-cast MPa. m1/2 at hypoeutectic compositions.
参考文献
| [1] | Edward L A .Niobium-base super alloys via powder metallurgy technology[J].Journal of The Minerals,Metals & Materials Society,1987,39(07):22. |
| [2] | Subramanian P R;Parthasarathy T.A;Mendiratta M.G;Dimiduk D.M .Compressive creep behavior of Nb5Si3[J].Scripta Metallurgica et Materialia,1995,32(08):1227. |
| [3] | Mendiratta M G;Dimiduk D M .Phase relation and transformation kinetics on the high Nb region of the Nb-Si system[J].Scripta Metallurgica et Materialia,1991,25(01):237. |
| [4] | Mendiratta M G;Dimiduk D M .Strength and toughness of a Nb/Nb5Si3 composite[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1993,24:501. |
| [5] | Jackson M R;Bewlay B.P;Rowe R.G .High-temperature refractory metal-intermetallic composites[J].Journal of The Minerals,Metals & Materials Society,1996,48:39. |
| [6] | Ashby M F;Blunt F.J;Bannister M .Flow characteristics of highly constrained metal wires[J].Acta Materialia,1989,7:1847. |
| [7] | Schlesinger M E;Okamoto H;Gokhale A B .[J].Journal of PHASE EQUILIBRIA,1993,14(04):502. |
| [8] | Gokhale A B;Abbaschian G J .The Mo-Si (Molybdenum-Silicon) system[J].Journal of Phase Equilibria,1991,12(04):493. |
| [9] | Kim W Y;Tanaka H;Kasama A .Microstructure and room temperature fracture toughness of Nb/Nb5Si3 in situ composites[J].Internetallics,2001,9(09):827. |
| [10] | Yi Tan;Hisao Tanaka;Chaoli Ma;Akio Kasama;Ryohei Tanaka;Yoshinao Mishima;Shuji Hanada .Solid-solution strengthening and high-temperature compressive strength of Nb-X alloys (X = Ta, V, Mo and W)[J].日本金属学会誌,2000(7):559-565. |
| [11] | Peters B C;Hendrickson A·A .Solid solution strengthening Nb-Ta and Nb-Mo alloy single crystals[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1970,1(08):2271. |
| [12] | Won-Yong Kim;Hisao Tanaka;Shuji Hanada .Microstructure and high temperature strength at 1773K of Nb_(ss)/Nb_5Si_3 composites alloyed with molybdenum[J].Intermetallics,2002(6):625-634. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%