采用硬度、腐蚀速率、剥落腐蚀、慢应变速率拉伸测试及透射电镜和差示扫描量热法研究预拉伸后时效制度对7050铝合金板材显微组织、硬度和抗腐蚀性能的影响.结果表明:峰时效合金硬度最大,抗腐蚀性能最差;过时效和回归再时效与峰时效相比,合金的硬度值减小,抗腐蚀性能变好;在高温+峰时效中的高温时效阶段,GP区发生回溶,有利于η′和η相的直接形核析出,晶内析出相长大、不均匀分布,合金硬度减小;晶界析出相粗化、断续分布,合金抗腐蚀性能提高.
@@@@The effects of aging after pre-stretching process on microstructure, hardness, and corrosion resistance of the 7050 aluminum alloy plate were investigated by means of hardness tests, corrosion rate tests, exfoliation corrosion tests, slow strain rate tensile(SSRT) tests, transmission electron microscopy and differential scanning calorimetry(DSC). The results indicate that the peak-aged 7050 aluminum alloy possesses the highest hardness, but its corrosion resistance is poor. The overaging and the retrogression and re-aging treatments lower the hardness, but improve the corrosion resistance of the 7050 aluminum alloy compared with the peak-aging treatment. At the high temperature aging stage of the high temperature and a subsequent low temperature aging, GP zone can be reversed, which is beneficial to the nucleation of η′ and η phases. Consequently, the precipitates within grains become coarser and distribute uniformly, leading to the decrease of hardness. Meanwhile, the precipitates at grain boundaries become coarser and discontinuous resulting in an improved corrosion resistance.
参考文献
| [1] | A. Heinz;A. Haszler;C. Keidel;S. Moldenhauer;R. Benedictus;W. S. Miller .Recent development in aluminium alloys for aerospace applications[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2000(1):102-107. |
| [2] | 王虎,李敬勇,刘志鹏.预拉伸对铝合金桶体焊接残余应力和变形影响的数值模拟[J].有色金属加工,2008(03):38-40. |
| [3] | D. Wang;Z.Y. Ma .Effect of pre-strain on microstructure and stress corrosion cracking of over-aged 7050 aluminum alloy[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2009(1/2):445-450. |
| [4] | Han, N.;Zhang, X.;Liu, S.;Ke, B.;Xin, X. .Effects of pre-stretching and ageing on the strength and fracture toughness of aluminum alloy 7050[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2011(10/11):3714-3721. |
| [5] | 韩念梅 .航空用7050铝合金板材断裂韧性的研究[D].长沙:中南大学,2011. |
| [6] | Wang, D;Ni, DR;Ma, ZY .Effect of pre-strain and two-step aging on microstructure and stress corrosion cracking of 7050 alloy[J].Materials Science and Engineering. A, Structural Materials: Properties, Microstructure and Processing,2008(1/2):360-366. |
| [7] | 林光磊.6063铝合金型材维氏硬度与强度的线性关系[J].轻合金加工技术,2002(01):29-31. |
| [8] | BIN-LUNG OU;JI-GANG YANG;MON-YU WEI .Effect of Homogenization and Aging Treatment on Mechanical Properties and Stress-Corrosion Cracking of 7050 Alloys[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2007(8):1760-1773. |
| [9] | 樊喜刚,蒋大鸣,孟庆昌,李念奎,孙兆霞.时效制度对7150铝合金组织和性能的影响[J].热加工工艺,2006(16):22-25. |
| [10] | F. Viana;A. M. P. Pinto;H. M. C. Santos;A. B. Lopes .Retrogression and re-ageing of 7075 aluminium alloy: microstructural characterization[J].Journal of Materials Processing Technology,1999(0):54-59. |
| [11] | LI Zhihui,XIONG Baiqing,ZHANG Yong'an,ZHU Baohong,WANG Feng,LIU Hongwei.Effects of the two-step ageing treatment on the microstructure and properties of 7B04 alloy pre-stretched thick plates[J].稀有金属（英文版）,2007(03):193-199. |
| [12] | 李松瑞;周善初.金属热处理[M].长沙:中南大学出版社,2005:221-240. |
| [13] | 韩念梅,张新明,刘胜胆,宋丰轩.预拉伸对7050铝合金断裂韧性的影响[J].中国有色金属学报,2010(11):2088-2093. |
| [14] | Kevin R. Cooper;R.G. Kelly .Crack tip chemistry and electrochemistry of environmental cracks in AA 7050[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2007(6):2636-2662. |
| [15] | Takano N .Hydrogen diffusion and embrittlement in 7075 aluminum alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2008(0):336-339. |
| [16] | 黄兰萍,陈康华,李松,宋旼.高温预析出后7055铝合金局部腐蚀性能和时效硬化[J].稀有金属材料与工程,2007(09):1628-1633. |
| [17] | Song RG;Dietzel W;Zhang BJ;Liu WJ;Tseng MK;Atrens A .Stress corrosion cracking and hydrogen embrittlement of an Al-Zn-Mg-Cu alloy[J].Acta materialia,2004(16):4727-4743. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%