在MgO系铸钛包埋料中加入α-Al2O3细粉,经1100℃热处理后,MgO和α-Al2O3可原位生成镁铝尖晶石,导致试样体积膨胀,显气孔率明显增加,耐压强度明显降低.当加入的α-Al2O3细粉为10%、20%(质量分数)时,α-Al2O3细粉几乎全部与MgO反应生成镁铝尖晶石,试样体积膨胀最明显,热膨胀率最大,可以很好地弥补钛铸件的冷却收缩.
参考文献
| [1] | Eliopoulos D;Zinelis S;Papadopoulos T .The effect of investment material type on the contamination zone and mechanical properties of commercially pure titanium castings.[J].The Journal of Prosthetic Dentistry,2005(6):539-548. |
| [2] | 陈治清.口腔材料学[M].北京:人民卫生出版社,2001:156. |
| [3] | Guilin Y;Nan L;Yousheng L;Yining W .The effects of different types of investments on the alpha-case layer of titanium castings.[J].The Journal of Prosthetic Dentistry,2007(3):157-164. |
| [4] | Spiros Zinelis .Surface and elemental alterations of dental alloys induced by electro discharge machining (EDM)[J].Dental materials,2007(5):601-607. |
| [5] | 阎俏梅,张建中.口腔铸钛包埋材料的研究进展[J].上海口腔医学,2001(01):76-78. |
| [6] | 王维邦.耐火材料工艺学[M].北京:冶金工业出版社,1994:146. |
| [7] | 马翔弘;刘玉英.烧结过程中原生尖晶石相的形成(膨胀与收缩)[J].国外耐火材料,1998(08):24. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%