Fe100-xPtx(x=30at.%-60at.% ) nanocomposite films were deposited on natural-oxidized Si(100) substrates by magnetron sputtering. The as-deposited films were annealed between 373 and 1073 K. In situ X-ray diffraction shows that the FePt nanocomposite films undergo a phase transformation from a disordered FCC phase to an ordered L10 phase between 673 and 773 K. The coercivity is 306 kA·m-1 whiles the average grain sizes is about 10 nm in the optimized FePt alloy film sample annealed at 673K. The adjustable coercivity and fine grain size suggest that this FePt nanocomposites system is suitable as recording media at extremely high areal density.
参考文献
| [1] | Farrow RFC.;Marks RF.;Toney MF.;Cebollada A.;Harp GR.;Weller D. .CONTROL OF THE AXIS OF CHEMICAL ORDERING AND MAGNETIC ANISOTROPY IN EPITAXIAL FEPT FILMS[J].Journal of Applied Physics,1996(8 Pt.2b):5967-5969. |
| [2] | Coffey K;Parker M A;Howard J K .High anisotropy L10 thin films for longitudinal recording[J].IEEE Transactions on Magnetics,1995,31:2737. |
| [3] | Jia Zhiyong;Kang Shishou;Shi Shifan;HarrellJ W et al.Size effect on L10 ordering and magnetic properties of chemically synthesized FePt and FePtAu nanoparticles[J].Journal of Applied Physics,2005,97:10J310. |
| [4] | Chang Hoi Park;Jong Gab Na;Pyung Woo Jang;Seong-Rae Lee .Effects of annealing condition on the structural and magnetic properties of FePt thin films[J].IEEE Transactions on Magnetics,1999(5):3034-3036. |
| [5] | Kuo PC.;Kuo CM.;Wu HC.;Yao YD. .Microstructure and magnetic properties of the (FePt)(100-x)Cr-x thin films[J].Journal of Applied Physics,2000(9 Pt.3):6146-6148. |
| [6] | Kim Han Jae;Lee Seong-Rae .Texture development and magnetic properties of sputter-deposited FePt-MgO nanocomposite films[J].Applied Physics A:Materials Science & Processing,2005,97:10H304. |
| [7] | Ding Y;Majetich SA .Size dependence, nucleation, and phase transformation of FePt nanoparticles[J].Applied physics letters,2005(2):2508-1-2508-3-0. |
| [8] | Müller Michael;Albe Karsten .Lattice Monte Carlo simulations of FePt nanoparticles:Influence of size,composition,and surface segregation on order-disorder phenomena[J].Physical Review B:Condensed Matter,2005,72:94203. |
| [9] | Whang S H;Feng Q;Gao Y O .Ordering deformation and microstructure in L10 type FePt[J].Pergamon Acta Mater,1998,18:6485. |
| [10] | Chen SC.;Lie CT.;Hua JT.;Kuo PC. .Microstructure and coercivity of granular FePt-AlN thin films[J].Journal of Magnetism and Magnetic Materials,2001(1/2):151-157. |
| [11] | Zeng Hao;Li Jing;Liu J P et al.Exchange-coupled nanocomposite magnets by nanoparticle self-assembly[J].NATURE,2002,420:395. |
| [12] | Simizu S.;Obermyer RT.;Zande B.;Chandhok VK.;Margolin A.;Sankar SG. .Exchange coupling in FePt permanent magnets[J].Journal of Applied Physics,2003(10 Pt.3):8134-8136. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%