利用透射电镜在室温变形的γ-TiAl基合金中研究了一种新的形变孪晶与α2片的交截机制.选区电子衍射和矩阵分析结果表明:γ基体中的形变孪晶切过α2片时,如果形变孪晶的宽度与α2片宽度相当,则α2片可以通过K1={3031},η1=1/18<10 16>的孪生机制来协调形变孪晶产生的切变.由于α2片与γ基体之间存在(0001)α2∥{111}γ,<1120>α2∥<011>γ的晶体位向关系,α2片的1/18<10 16>{3031}切变矢量等价于形变孪晶的切变矢量1/6<112]{111},因此形变孪晶产生的切变可完整地切过α2片而不需要交截区附近γ基体中其它滑移系或孪晶系开动来辅助协调变形.
参考文献
| [1] | Apple F;Wagner R .[J].Materials Science and Engineering,1998,R22:187. |
| [2] | Inui H;Nakamura A;Oh M H;Yamaguchi M .[J].Philosophical Magazine A:Physics of Condensed Matter:Structure,Defects and Mechanical Properties,1992,66(04):557. |
| [3] | Inui H et al.[J].Philosophical Magazine A:Physics of Condensed Matter:Structure,Defects and Mechanical Properties,1995,72(06):1609. |
| [4] | Kishida K;Inui H;Yamaguchi M .[J].Philosophical Magazine A:Physics of Condensed Matter:Structure,Defects and Mechanical Properties,1998,78(01):1. |
| [5] | 王继杰,蒋敏,郝士明.γ-TiAl基双相合金片层组织不连续粗化的驱动力与动力学[J].稀有金属材料与工程,1998(03):161-164. |
| [6] | 郭富安,Vincent JI,张永刚,陈昌麒.γ-TiAl基金属间化合物合金的显微组织与内应力研究[J].稀有金属材料与工程,2001(02):105-108. |
| [7] | Zhang Y G;Tichelaar F D;Schapink F W;Chaturvedi M C .[J].Materials Science and Engineering,1996,219A:162. |
| [8] | Sun Y Q;Hazzledine P M;Christian J W .[J].Philosophical Magazine A:Physics of Condensed Matter:Structure,Defects and Mechanical Properties,1993,68(03):471. |
| [9] | Sun Y Q;Hazzledine P M;Christian J W .[J].Philosophical Magazine A:Physics of Condensed Matter:Structure,Defects and Mechanical Properties,1993,68(03):495. |
| [10] | Wardle B S;Phan I;Hug G .[J].Philosophical Magazine A:Physics of Condensed Matter:Structure,Defects and Mechanical Properties,1993,67(02):497. |
| [11] | Zhang Y G et al.[J].Philosophical Magazine A:Physics of Condensed Matter:Structure,Defects and Mechanical Properties,1993,68(05):915. |
| [12] | Murray J L.Massalski T B ed. Phase Diagrams of BinaryTitanium Alloys[A].Ohio:Am Soc Metals,Metals Park,1986:12. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%