研究了轧制温度和热处理制度对TB9钛合金棒材显微组织及力学性能的影响。结果表明：在800、850、930℃下轧制的TB9钛合金棒材经810℃×30 min／WQ固溶后，显微组织均为等轴β组织，930℃下轧制的棒材组织更加均匀，轧制温度对棒材固溶后的力学性能影响较小。经510℃×12 h／AC时效处理后，棒材的强度和塑性等综合性能随轧制温度的升高变化不大，抗拉强度全部大于1300 MPa，屈服强度大于1200 MPa，延伸率大于10％，能够满足某零件对材料的要求。此外， TB9钛合金的强度随时效温度的上升而减小，而塑性逐渐增加。
The effects of rolling temperature and heat treatment on microstructures and mechanical properties of TB 9 titanium alloy rods were studied in this research .The results indicate that the microstructure of the alloy is equiaxed βgrain when rolled at 800 ℃, 850 ℃and 930 ℃and then solid solutioned at 810 ℃for 30 minutes.The grain size is uniform when the rolling temperature is 930 ℃.Rolling temperature has little influence on microstructures and mechanical properties of solid solutioned TB 9 titanium alloy rods .After aged at 510 ℃ for 12 hours, the rods with different rolling temperatures have almost coherent mechanical properties , the tensile strength is above 1 300 MPa, the yield strength is above 1 200 MPa, and the ductility is above 10%, which can match the application required . Otherwise , as the aging temperature rised , the tensile strength of TB 9 titanium alloy rods is reduced and the ductility is increased.
参考文献
| [1] | 莱茵斯C;皮特尔斯M;陈振华.钛及钛合金[M].北京:化学出版社,2005:240-253. |
| [2] | Mantani Y;Tajima M.Phase transformation of quenched α″martensite by aging in Ti-Nb alloys[J].MATERIALS SCIENCE & ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2006(438/440):315-319. |
| [3] | 稀有金属材料加工手册编写组.稀有金属材料加工手册[M].北京:冶金工业出版社,1984:30. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%