以Ag-Cu合金废触点制备CuCl2和AgCl,采用葡萄糖预还原-水合肼二次还原法制备超细铜粉、氨-肼还原法制备超细银粉.结果表明:在反应温度为70 ℃,加入适量PVP和苯并三氮唑作为分散剂和抗氧化剂的条件下,所得微米级铜粉的粒度在0.3～0.6 μm,粒度分布范围小,纯度高于99.9%.经3个月的抗氧化试验表明,所得铜粉产品的抗氧化性能较高.一定时间的球磨是氨-肼还原法制备超细银粉的关键,经24 h湿法球磨后干燥所得银粉的粒度为1.90 μm,分布均匀.
参考文献
| [1] | Dragieva I D;Stoynov Z B;Klabunde K J .[J].Scripta Materialia,2001,44:2187. |
| [2] | 周全法,蒋萍萍,朱雯,赵德建.抗氧化纳米铜粉的制备及表征[J].稀有金属材料与工程,2004(02):179-182. |
| [3] | Rao R S;Walters A B;Vannice M A .[J].Journal of Physical Chemistry B,2005,109:2086. |
| [4] | Kobiyama M;Inami T;Okuda S .[J].Scripta Materialia,2001,44:1547. |
| [5] | Cason J P;Miller M E;Thompson J B et al.[J].Journal of Physical Chemistry B,2001,105:2297. |
| [6] | Ding J et al.[J].Journal of Alloys and Compounds,1996,234:L1. |
| [7] | 王琪;周全法;黄红缨 .[J].Gold(黄金),2005,26(11):47. |
| [8] | 周全法;王琪;谈永祥.[J].Recycling Research (再生资源研究),2001(01):16. |
| [9] | 周全法.The Deepen Processing and Application of Precious Metals(贵金属深加工及其应用)[M].北京:化学工业出版社,2002:66. |
| [10] | 李林艳;徐盛明;杜多林 et al.[J].Rare Metal Materials and Engineering (稀有金属材料与工程),2007,36(03):230. |
| [11] | 东建中;刘英 .[J].Powder Metallurgy Industry (粉末冶金工业),1995,2(26):57. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%