将9,10-蒽醌（AQ）通过升华法填充在介孔炭（MC）的孔中,制备出蒽醌/介孔炭寄生型复合物。用TG/DSC、SEM、氮吸附等方法对介孔炭及复合材料进行了表征,应用恒流充放电、循环伏安法、交流阻抗等测试手段对复合材料的电化学性能进行了测试。结果表明炭/醌复合电极的比容量和循环性能较蒽醌电极有了很大程度的提高。其中蒽醌填充量为75%的复合材料首次放电比容量达到216mAh/g,50次循环之后,比容量仍有76mAh/g,是蒽醌电极比容量的2倍。
The mesoporous carbon（MC）/AQ parasitic composite was synthesized by filling 9,10-anthraquinone into pores of MC with sublimation.The composite was charactered by the methods of TDA/DSC,SEM and N2 adsorption.The electrochemical performance of the composite was investigated by the methods of galvanostatic discharge/charge and cyclic voltammetry.The results indicated that the specific capacity and cycle life of the composite was increased.The initial discharge specific capacity of the composite（75% AQ contained） arrived at 216mAh/g,after 50 cycles,the specific capacity maintained 76mAh/g,which was twice as great as AQ electrode＇s.
参考文献
| [1] | M.Stanley Whittingham .Lithium Batteries and Cathode Materials[J].Chemical Reviews,2004(10):4271-4301. |
| [2] | Chen, HY;Armand, M;Courty, M;Jiang, M;Grey, CP;Dolhem, F;Tarascon, JM;Poizot, P .Lithium Salt of Tetrahydroxybenzoquinone: Toward the Development of a Sustainable Li-Ion Battery[J].Journal of the American Chemical Society,2009(25):8984-8988. |
| [3] | Song ZP;Zhan H;Zhou YH .Anthraquinone based polymer as high performance cathode material for rechargeable lithium batteries[J].Chemical communications,2009(4):448-450. |
| [4] | Sang-Eun Cheon;Soo-Seok Choi;Ji-Seong Han .Capacity Fading Mechanisms on Cycling a High-Capacity Secondary Sulfur Cathode[J].Journal of the Electrochemical Society,2004(12):A2067-A2073. |
| [5] | 王维坤,王安邦,曹高萍,杨裕生.锂电池正极材料多硫化碳炔的制备及电化学性能[J].应用化学,2005(04):367-371. |
| [6] | J. L. Wang;J. Yang;J. Y. Xie;N. X. Xu;Y. Li .Sulfur-carbon nano-composite as cathode for rechargeable lithium battery based on gel electrolyte[J].Electrochemistry communications,2002(6):499-502. |
| [7] | 赵春荣,王维坤,刘荣江,杨裕生.常温下真空浸渍制备的LMC/S复合材料[J].电池,2010(01):6-9. |
| [8] | Chunrong Zhao;Weikun Wang;Zhongbao Yu .Nano-CaCO3 as template for preparation of disordered large mesoporous carbon with hierarchical porosities[J].Journal of Materials Chemistry: An Interdisciplinary Journal dealing with Synthesis, Structures, Properties and Applications of Materials, Particulary Those Associated with Advanced Technology,2010(5):976-980. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%