采用正交试验法对NdFeB磁体表面化学镀镍磷合金的工艺进行了优化,测量了镀层和基体在3.5%(ω)NaCl溶液、10%(ψ)盐酸和20%(ω)NaOH溶液中的腐蚀速度,以及在3.5%NaCl溶液中的极化曲线和电化学阻抗谱,对比分析了在酸性和碱性条件下所得Ni-P镀层的结构和表面形貌.结果表明,采用EIS谱图及等效电路模型可对镀层和磁体在介质中的电化学参数进行拟合分析,化学镀Ni-P合金能够显著改善NdFeB磁体的耐腐蚀性能,且酸性条件下所获得的镀层为非晶态结构,表面胞状组织呈密集连续分布,耐腐蚀性能更佳.
参考文献
| [1] | Kim A.S.;Camp F.E. .A high performance Nd-Fe-B magnet with improved corrosion resistance[J].IEEE Transactions on Magnetics,1992(5):2151-2153. |
| [2] | 王海林,何庆琳.粘结型Nd-Fe-B永磁体化学镀镍[J].电镀与精饰,1999(02):16-18. |
| [3] | 周琦.烧结型NdFeB永磁体的镀前处理工艺[J].电镀与精饰,2001(03):34-37. |
| [4] | El-Aziz AM.;Gutfleisch O.;Gebert A.;Schultz L.;Kirchner A. .Investigations of the corrosion behaviour of nanocrystalline Nd-Fe-B hot pressed magnets[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2000(2):299-304. |
| [5] | Assis O B G;Sinka V;Ferrante M et al.[J].Journal of Alloys and Compounds,1995,218(02):263. |
| [6] | Kim AS.;Lizzi T.;Camp FE. .HYDROGEN INDUCED CORROSION MECHANISM IN NDFEB MAGNETS[J].Journal of Applied Physics,1996(8 Pt.2a):4840-4842. |
| [7] | Li Y;Evans H E;Harris I R et al.[J].Oxidation of Metals,2003,59(1-2):167. |
| [8] | Hu Y;Aindow M;Jones L P et al.[J].Journal of Alloys and Compounds,2003,351(1-2):299. |
| [9] | Walton A.;Speight J.D. .A zinc coating method for Nd-Fe-B magnets[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2000(1/2):253-261. |
| [10] | Blackwood DJ.;Huang YZ.;Tan CK.;Balakrisnan B. .Influence of the chemical composition of the plating solution on the ability of nickel coatings to protect Nd2Fe14B magnets against corrosion[J].Journal of Magnetism and Magnetic Materials,2001(2):103-111. |
| [11] | 李军,刘颖,高升吉,涂铭旌.粘结钕铁硼磁体阴极电泳工艺研究[J].腐蚀科学与防护技术,2005(02):121-124. |
| [12] | 郑华均,郑国渠,马淳安.化学镀镍磷合金工艺研究及其在钕铁硼永磁体抗蚀上的应用[J].表面技术,2002(02):42-45. |
| [13] | Liu R;Gao C;Yang J .[J].Metal Finishing,2002,100(03):34. |
| [14] | 饶厚曾,李国华.钕铁硼永磁材料碱性化学镀Ni-P[J].材料保护,2000(07):15. |
| [15] | 廖海星,喻克雄.双层镍-磷化学镀研究[J].华中师范大学学报(自然科学版),2003(02):197-198,203. |
| [16] | Guojin L;Giovanni Z .[J].Electrochimica Acta,2002,47(18):2969. |
| [17] | Taheri R .Evaluation of Electroless Nickel-phosphorus(EN)Coatings[D].Saskatchewan:The University of Saskatchewan,2003. |
| [18] | 何少华;文竹青;娄涛.试验设计与数据处理[M].长沙:国防科技大学出版社,2002:70,220. |
| [19] | 杨永德;杜青山 .[J].电镀与环保,1995,15(06):12. |
| [20] | Zhang X;van den Bos C;Sloof WG;Hovestad A;Terryn H;de Wit JHW .Comparison of the morphology and corrosion performance of Cr(VI)- and Cr(III)-based conversion coatings on zinc[J].Surface & Coatings Technology,2005(1):92-104. |
| [21] | Sankara Narayanan T S N;Baskaran I;Krishnaveni K et al.[J].Surface and Coatings Technology,2006,200(01):3438. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%