研究了LaNi4-xFeCrx(x=0.2、0.4、0.6、0.8、1.0)合金中Cr替代Ni对显微组织及电化学性能的影响.研究表明,Cr的加入均使合金析出第二相,降低电化学放电容量,提高循环稳定性.合金的高倍率放电性能随x增加先增大后缓慢下降.
参考文献
| [1] | 李世群,陈立新,郭蕊,张书凯,应窕,雷永泉.RENi4.3-xCoxMn0.4Al0.3贮氢合金（x=0.5～1.3）的相结构及高温电化学性能[J].稀有金属材料与工程,2003(03):228-231. |
| [2] | Hu WK .Studies on cobalt-free AB sub 5 -type hydrogen storage alloys[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,1999(1/2):299-305. |
| [3] | 陈立新.贮氢电极合金Ml（NiMnTi）4.2Co0.8-xFex（x=0～0.8）的电化学性能[J].稀有金属材料与工程,1999(05):302. |
| [4] | Chiaki Iwakura;Kazuhiro Ohkawa;Hiroshi Senoh;Hiroshi Inoue .Electrochemical and crystallographic characterization of Co-free hydrogen storage alloys for use in nickel-metal hydride batteries[J].Electrochimica Acta,2001(28):4383-4388. |
| [5] | 魏范松,雷永泉,陈立新,廖彬,应窕,葛红卫,吕光烈.低Co贮氢合金ReNi3.5Co0.3Mn0.3Al0.4Fe0.5-xSnx（x=0～0.4）的相结构和电化学性能[J].材料科学与工程学报,2003(03):323-326. |
| [6] | Khaldi C;Mathlouthi H;Lamloumi J et al.[J].International Journal of Hydrogen Energy,2004,29:307-311. |
| [7] | Meli F;Züttel A;Schlapbach L et al.[J].Journal of Alloys and Compounds,1995,231:639-644. |
| [8] | 张晓燕,陈云贵,陶明大,吴朝玲,宋永贵.LaNi5-xFex（x=1～1.8）合金相结构及电化学性能[J].稀有金属材料与工程,2008(08):1388-1391. |
| [9] | 吕俊霞,周海,庄应烘,刘敬旗.La-Ni-Cr三元系600℃等温截面的相关系[J].稀有金属材料与工程,2005(05):758-760. |
| [10] | Sakai T;Oguro K;Miyamura H et al.[J].Journal of the Less-Common Metals,1990,161:193-202. |
| [11] | Van Mal H H;Buschow K H J;Miedema A R .[J].Journal of the Less-Common Metals,1974,35:65-76. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%