MoSx coatings were prepared by bipolar-pulse DC unbalanced magnetron-sputtering system with the variation of coating thickness at different Ar pressures. The composition and surface morphology were determined by using energy dispersive X-ray and scanning electron microscopy; the structural characterisation was analyzed by X-ray diffraction. The friction and wear properties were investigated by fretting tests in air with less than 10% and 50%relative humidity. At 0.40 Pa pressure, (002) basal plane orientation was formed throughout the coatings. At 0.88Pa and 1.60 Pa pressures, (002) basal plane orientation was only noticed in the first stage of coating growth (around 0.20 μm in thickness), and then edge orientations with their basal planes perpendicular to the surface would be evolved in the coatings. Humidity has a minor influence on the coatings that have (002) basal plane orientation,whereas the tribological properties of MoSs coatings with edge orientations are greatly affected by humidity. The mechanisms of coating growth and friction and wear processes are discussed.
参考文献
| [1] | M R Hilton;P D Fleischauer.[J].Surface and Coatings Technology,1992:54-55,435. |
| [2] | T Spalvins .[J].THIN SOLID FILMS,1982,96:17. |
| [3] | T Spalvins .[J].THIN SOLID FILMS,1980,73:291. |
| [4] | B C Stupp .[J].THIN SOLID FILMS,1981,74:257. |
| [5] | R I Christy .[J].THIN SOLID FILMS,1980,73:299. |
| [6] | T Spalvins .[J].Journal of Vacuum Science and Technology A-Vacuum Surfaces and Films,1987,a5:212. |
| [7] | T Spalvins .[J].Thin Solid Films,1984,118:375. |
| [8] | J S Zabinski;M S Donley;S D Walck;T R Schneider, N T McDevitt .[J].Tribology Transactions,1995,38(04):894. |
| [9] | J Wang;W Lauwerens;E Wieers;L M Stals, J He ,J P Celis .[J].Surface and Coatings Technology,2001,139:143. |
| [10] | B Window;N Savvides .[J].Journal of Vacuum Science and Technology,1986,A(04):453. |
| [11] | H. Mohrbacher;J.-P. Celis;J. R. Roos .Laboratory testing of displacement and load induced fretting[J].Tribology International,1995(5):269-278. |
| [12] | p Campbell;J P Celis;J R Roos;O VanDer Biest .[J].Wear,1994,174:174,47. |
| [13] | D N Dunn;L E Seitzman;I L Signer .[J].Journal of Materials Research,1997,12(05):1191. |
| [14] | E. de Wit;B. Blanpain;L. Froyen;J. -P.Celis .The tribochemical behaviour of TiN-coatings during fretting wear[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,1998(2):215-224. |
| [15] | Xiaoling Zhang;V Roumen;Jihui Wang.Proceedings of the 5th Annual Meeting of the Belgian Ceramic Society, Sept. 15, Liege[J].Belgium,2000:230. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%