采用Cr3+离子镀液,以SUS304钢为阳极和Fe离子源,在4Cr10Si2Mo钢表面电沉积了非晶态Cr-Fe-C三元合金镀层,之后在不同温度下对镀层进行退火.通过XRD、EDS分析以及硬度实验和极化曲线测量,研究了镀层的成分、组织和性能.结果表明:非晶态Cr-Fe-C镀层主要由(质量分数)65.8%Cr,27%Fe和6.58%C组成,镀层中无显微裂纹,在3%NaCl溶液中的耐蚀性明显优于SUS304不锈钢.镀层硬度随退火温度的升高而增大,600℃退火时硬度达到最高值18000 MPa.硬度随温度的变化,与镀层中相继出现Cr原子的偏聚、Cr3C2、Cr7C3、Cr23C6和Cr2O3等化合物有关.
参考文献
| [1] | Shigeo Hoshino;Laitinen Hebert A;Hoflund Gar B .[J].Electrochemical Science and Technology,1986,133(03):681. |
| [2] | Matsufumi Takaya;Masahisa Matsunaga;Tetsuo Otaka .[J].J Met Finish Jpn,1986,37(10):624. |
| [3] | Yoshiomi Aoyagi;Masamichi Kowaka .[J].J Met Finish Jpn,1989,40(03):453. |
| [4] | Rung-Ywan Tsai;Shinn-Tyan Wu .[J].Journal of the Electrochemical Society,1991,138(04):1006. |
| [5] | Prznioslo R;Wagner J;Natter H et al.[J].Journal of Alloys and Compounds,2001,328:259. |
| [6] | Tsutomu Morikawa;Masayuki Yokoi;Seiichiro Eguchi et al.[J].J Met Finish Jpn,1991,42(01):100. |
| [7] | Tohru Watanabe .[J].Materials Science and Engineering,1994,Al70-A180:193. |
| [8] | 李惠东.从三价铬镀液中电沉积可替代硬铬镀层的铬合金镀层[J].电化学,1998(02):217. |
| [9] | Japanese Society of Metal.Metals Date Handbook[M].Tokyo:Maluzen Press,1991:14. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%