模拟了海底管线的腐蚀情况，并利用极化曲线及电化学阻抗技术，研究了试验六个月情况下试片的腐蚀规律。结果表明，试样在开放的海水介质中靠近裂缝处腐蚀速率较快，远离裂缝处腐蚀速率相对较慢。而在模拟海底的试验环境下，管线腐蚀规律与开放海水中测量的结果相反，即靠近裂缝处腐蚀相对较慢，，远离裂缝处腐蚀相对较快。
Corrosion law of submarine pipeline was studied by polarization curves and electrochemical impedance spectroscopy （EIS）. The results showed that in the open seawater corrosion rate of samples was rapid and severe near the cracks, but was relatively light the corrosion away from cracks. In the simulated seabed testing environment, an opposite corrosion law was shown, the nearer the samples from the cracks, the slower the corrosion rate.
参考文献
| [1] | 舒勇,熊春明,张建军.高含水期油田集输系统腐蚀结垢原因及综合防治技术[J].腐蚀科学与防护技术,2010(01):67-70. |
| [2] | 侯涛,安国亭.海底管道损伤的原因分析及修复[J].中国海洋平台,2002(04):37-39. |
| [3] | Mark Burton .Options for deepwater repair of pipes and flanges[J].Pipes & Pipelines International,2001(3):42-44,49-0. |
| [4] | 周晶,陈严飞,李昕,冯新,范颖芳.复杂荷载作用下海底腐蚀管线破坏机理研究进展[J].海洋工程,2008(01):127-136. |
| [5] | 刘永杰,邓卫东,党舸,徐化奎,董建畅,郭海军.南海番禺气田海底管线内腐蚀评价与预测[J].石油化工腐蚀与防护,2008(04):20-22. |
| [6] | Luo LR;Zhang ZJ .Sensors based on galvanic cell generated electrochemiluminescence and its application[J].Analytica chimica acta,2006(1):14-17. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%